Pottery-Stone Database / Fukami Vein

Fukami Vein, 17 samples

Results of TGA & Colors of the powder samples after measuring

Results of TMA & Colors of the sintered samples after measuring

No. Name Sampling date Vein or deposit Mining place Mining company Sampling place Grade or sort
173 HFIH_01S March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/right/forth working face Henshoku(discoloration)
174 HFI2_02A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/right/forth working face Second grade
175 HFIN_03A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/right/forth working face Onikawa(iron oxide rich phase) clay
176 HFIN_04A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/right/forth working face Fault clay
177 HFIN_06A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/left/forth working face Fault clay
178 HFIN_08A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/left/third working face Fault clay
179 HFI1_09S March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/left/second working face First grade, SK29
180 HFI3S10A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/left/second working face Third grade, Shima(stripes), SK28
181 HFI3_12A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Dressing plant Third grade, for insulator
182 HFI1_13A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Dressing plant First grade, special grade in other vein
183 HFI4_14A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Dressing plant Waste rock, separable fourth grade
194 SFD1_01A March 26, 1981 Fukami V. Fukami Shin-ei Tohseki Stock yard First grade
195 SFDH_02A March 26, 1981 Fukami V. Fukami Shin-ei Tohseki Stock yard Henshoku(discoloration)
196 SFD3_03A March 26, 1981 Fukami V. Fukami Shin-ei Tohseki Stock yard Third grade, small rock
197 SFD3_04A March 26, 1981 Fukami V. Fukami Shin-ei Tohseki Stock yard Third grade A
198 SFD__05A March 26, 1981 Fukami V. Fukami Shin-ei Tohseki Inside drift White color, rough
199 SFD__06A March 26, 1981 Fukami V. Fukami Shin-ei Tohseki Inside drift Colored, fine

No.	Name	Sampling date	Vein or deposit	Mining place	Mining company	Sampling place	Grade or sort
173	HFIH_01S	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/right/forth working face	Henshoku(discoloration)
174	HFI2_02A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/right/forth working face	Second grade
175	HFIN_03A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/right/forth working face	Onikawa(iron oxide rich phase) clay
176	HFIN_04A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/right/forth working face	Fault clay
177	HFIN_06A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/left/forth working face	Fault clay
178	HFIN_08A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/left/third working face	Fault clay
179	HFI1_09S	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/left/second working face	First grade, SK29
180	HFI3S10A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/left/second working face	Third grade, Shima(stripes), SK28
181	HFI3_12A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Dressing plant	Third grade, for insulator
182	HFI1_13A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Dressing plant	First grade, special grade in other vein
183	HFI4_14A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Dressing plant	Waste rock, separable fourth grade
194	SFD1_01A	March 26, 1981	Fukami V.	Fukami	Shin-ei Tohseki	Stock yard	First grade
195	SFDH_02A	March 26, 1981	Fukami V.	Fukami	Shin-ei Tohseki	Stock yard	Henshoku(discoloration)
196	SFD3_03A	March 26, 1981	Fukami V.	Fukami	Shin-ei Tohseki	Stock yard	Third grade, small rock
197	SFD3_04A	March 26, 1981	Fukami V.	Fukami	Shin-ei Tohseki	Stock yard	Third grade A
198	SFD__05A	March 26, 1981	Fukami V.	Fukami	Shin-ei Tohseki	Inside drift	White color, rough
199	SFD__06A	March 26, 1981	Fukami V.	Fukami	Shin-ei Tohseki	Inside drift	Colored, fine

Colors of the milled samples
No. Name X Y Z Whiteness
(Hunter) L a b Whiteness
(Lab)
173 HFIH_01S 85.82 86.80 97.60 82.71 93.17 1.38 3.11 92.37
174 HFI2_02A 83.40 83.93 84.68 71.76 91.61 2.17 9.33 87.27
175 HFIN_03A 61.51 59.73 40.41 34.25 77.29 6.82 23.10 66.89
176 HFIN_04A 84.36 85.19 87.66 74.29 92.30 1.63 8.30 88.56
177 HFIN_06A 57.55 57.42 50.92 43.15 75.78 2.96 13.20 72.25
178 HFIN_08A 76.66 76.30 66.22 56.12 87.35 3.79 16.20 79.10
179 HFI1_09S 86.75 87.52 98.42 83.41 93.55 1.81 3.11 92.62
180 HFI3S10A 79.25 79.23 71.27 60.40 89.01 3.16 14.84 81.27
181 HFI3_12A 74.86 74.12 66.23 56.13 86.09 4.55 14.65 79.29
182 HFI1_13A 89.09 89.49 101.18 85.75 94.60 2.56 2.80 93.40
183 HFI4_14A 71.46 70.45 58.98 49.98 83.93 5.09 17.09 76.00
194 SFD1_01A 81.89 81.71 79.05 66.99 90.39 3.52 11.43 84.66
195 SFDH_02A 79.43 79.21 77.96 66.07 89.00 3.56 10.36 84.47
196 SFD3_03A 74.08 73.32 65.21 55.26 85.63 4.58 14.79 78.88
197 SFD3_04A 75.76 75.23 66.38 56.25 86.74 4.13 15.34 79.31
198 SFD__05A 86.33 86.68 95.61 81.03 93.10 2.59 4.28 91.48
199 SFD__06A 68.36 68.49 63.09 53.47 82.76 2.62 12.73 78.41

Colors of the milled samples
No.	Name	X	Y	Z	Whiteness (Hunter)	L	a	b	Whiteness (Lab)
173	HFIH_01S	85.82	86.80	97.60	82.71	93.17	1.38	3.11	92.37
174	HFI2_02A	83.40	83.93	84.68	71.76	91.61	2.17	9.33	87.27
175	HFIN_03A	61.51	59.73	40.41	34.25	77.29	6.82	23.10	66.89
176	HFIN_04A	84.36	85.19	87.66	74.29	92.30	1.63	8.30	88.56
177	HFIN_06A	57.55	57.42	50.92	43.15	75.78	2.96	13.20	72.25
178	HFIN_08A	76.66	76.30	66.22	56.12	87.35	3.79	16.20	79.10
179	HFI1_09S	86.75	87.52	98.42	83.41	93.55	1.81	3.11	92.62
180	HFI3S10A	79.25	79.23	71.27	60.40	89.01	3.16	14.84	81.27
181	HFI3_12A	74.86	74.12	66.23	56.13	86.09	4.55	14.65	79.29
182	HFI1_13A	89.09	89.49	101.18	85.75	94.60	2.56	2.80	93.40
183	HFI4_14A	71.46	70.45	58.98	49.98	83.93	5.09	17.09	76.00
194	SFD1_01A	81.89	81.71	79.05	66.99	90.39	3.52	11.43	84.66
195	SFDH_02A	79.43	79.21	77.96	66.07	89.00	3.56	10.36	84.47
196	SFD3_03A	74.08	73.32	65.21	55.26	85.63	4.58	14.79	78.88
197	SFD3_04A	75.76	75.23	66.38	56.25	86.74	4.13	15.34	79.31
198	SFD__05A	86.33	86.68	95.61	81.03	93.10	2.59	4.28	91.48
199	SFD__06A	68.36	68.49	63.09	53.47	82.76	2.62	12.73	78.41

Chemical compositions (wt%)
No. Name SiO₂ Al₂O₃ Fe₂O₃ TiO₂ CaO MgO Na₂O K₂O Ig.loss
173 HFIH_01S 79.03 14.87 0.20 0.04 0.05 0.13 0.07 0.48 4.75
174 HFI2_02A 76.87 16.25 0.29 0.04 0.09 0.11 0.09 0.73 5.07
175 HFIN_03A 77.74 14.72 1.65 0.03 0.08 0.08 0.06 0.52 4.72
176 HFIN_04A 78.50 14.97 0.39 0.04 0.13 0.15 0.07 0.36 4.67
177 HFIN_06A 78.63 14.14 0.86 0.03 0.12 0.18 0.14 1.11 4.21
178 HFIN_08A 78.94 14.54 0.68 0.03 0.08 0.08 0.08 0.76 4.40
179 HFI1_09S 79.01 14.90 0.18 0.04 0.04 0.06 0.10 0.49 4.78
180 HFI3S10A 76.78 15.77 0.39 0.04 0.07 0.07 0.21 1.88 4.50
181 HFI3_12A 77.37 14.92 0.64 0.04 0.10 0.06 0.34 2.15 3.99
182 HFI1_13A 77.72 15.94 0.20 0.04 0.11 0.07 0.05 0.39 4.90
183 HFI4_14A 78.82 14.62 0.66 0.03 0.07 0.05 0.15 1.09 4.19
194 SFD1_01A 79.81 14.64 0.27 0.13 0.05 0.07 0.03 0.33 4.40
195 SFDH_02A 78.80 15.06 0.37 0.04 0.07 0.10 0.06 0.63 4.52
196 SFD3_03A 78.43 14.92 0.56 0.03 0.07 0.10 0.12 1.04 4.33
197 SFD3_04A 79.48 14.54 0.46 0.03 0.06 0.07 0.04 0.60 4.35
198 SFD__05A 78.78 15.34 0.16 0.04 0.06 0.10 0.05 0.43 4.57
199 SFD__06A 78.20 14.94 1.01 0.04 0.08 0.16 0.02 0.39 4.69

Chemical compositions (wt%)
No.	Name	SiO₂	Al₂O₃	Fe₂O₃	TiO₂	CaO	MgO	Na₂O	K₂O	Ig.loss
173	HFIH_01S	79.03	14.87	0.20	0.04	0.05	0.13	0.07	0.48	4.75
174	HFI2_02A	76.87	16.25	0.29	0.04	0.09	0.11	0.09	0.73	5.07
175	HFIN_03A	77.74	14.72	1.65	0.03	0.08	0.08	0.06	0.52	4.72
176	HFIN_04A	78.50	14.97	0.39	0.04	0.13	0.15	0.07	0.36	4.67
177	HFIN_06A	78.63	14.14	0.86	0.03	0.12	0.18	0.14	1.11	4.21
178	HFIN_08A	78.94	14.54	0.68	0.03	0.08	0.08	0.08	0.76	4.40
179	HFI1_09S	79.01	14.90	0.18	0.04	0.04	0.06	0.10	0.49	4.78
180	HFI3S10A	76.78	15.77	0.39	0.04	0.07	0.07	0.21	1.88	4.50
181	HFI3_12A	77.37	14.92	0.64	0.04	0.10	0.06	0.34	2.15	3.99
182	HFI1_13A	77.72	15.94	0.20	0.04	0.11	0.07	0.05	0.39	4.90
183	HFI4_14A	78.82	14.62	0.66	0.03	0.07	0.05	0.15	1.09	4.19
194	SFD1_01A	79.81	14.64	0.27	0.13	0.05	0.07	0.03	0.33	4.40
195	SFDH_02A	78.80	15.06	0.37	0.04	0.07	0.10	0.06	0.63	4.52
196	SFD3_03A	78.43	14.92	0.56	0.03	0.07	0.10	0.12	1.04	4.33
197	SFD3_04A	79.48	14.54	0.46	0.03	0.06	0.07	0.04	0.60	4.35
198	SFD__05A	78.78	15.34	0.16	0.04	0.06	0.10	0.05	0.43	4.57
199	SFD__06A	78.20	14.94	1.01	0.04	0.08	0.16	0.02	0.39	4.69

Mineral compositions (wt%)
No. Name Quartz Sericite Kaolin mineral Feldspar Calcite Siderite
173 HFIH_01S 61.80 0.01 37.69 0.50 0.00 0.00
174 HFI2_02A 56.78 5.82 36.90 0.50 0.00 0.00
175 HFIN_03A 61.38 5.36 32.68 0.50 0.08 0.00
176 HFIN_04A 58.50 9.50 31.08 0.63 0.14 0.15
177 HFIN_06A 54.58 17.06 27.78 0.50 0.00 0.08
178 HFIN_08A 54.10 2.01 43.28 0.50 0.00 0.11
179 HFI1_09S 62.20 0.01 36.55 1.04 0.00 0.20
180 HFI3S10A 53.06 12.78 33.48 0.50 0.18 0.00
181 HFI3_12A 47.02 27.65 24.70 0.61 0.00 0.02
182 HFI1_13A 57.73 11.30 30.28 0.66 0.00 0.03
183 HFI4_14A 52.69 13.37 33.13 0.68 0.13 0.00
194 SFD1_01A 65.27 0.01 34.16 0.50 0.00 0.06
195 SFDH_02A 56.48 11.40 31.54 0.50 0.00 0.08
196 SFD3_03A 54.63 14.47 30.28 0.50 0.09 0.03
197 SFD3_04A 58.27 9.17 31.77 0.50 0.29 0.00
198 SFD__05A 57.98 0.01 41.34 0.55 0.01 0.11
199 SFD__06A 55.03 8.26 35.76 0.57 0.00 0.38

Mineral compositions (wt%)
No.	Name	Quartz	Sericite	Kaolin mineral	Feldspar	Calcite	Siderite
173	HFIH_01S	61.80	0.01	37.69	0.50	0.00	0.00
174	HFI2_02A	56.78	5.82	36.90	0.50	0.00	0.00
175	HFIN_03A	61.38	5.36	32.68	0.50	0.08	0.00
176	HFIN_04A	58.50	9.50	31.08	0.63	0.14	0.15
177	HFIN_06A	54.58	17.06	27.78	0.50	0.00	0.08
178	HFIN_08A	54.10	2.01	43.28	0.50	0.00	0.11
179	HFI1_09S	62.20	0.01	36.55	1.04	0.00	0.20
180	HFI3S10A	53.06	12.78	33.48	0.50	0.18	0.00
181	HFI3_12A	47.02	27.65	24.70	0.61	0.00	0.02
182	HFI1_13A	57.73	11.30	30.28	0.66	0.00	0.03
183	HFI4_14A	52.69	13.37	33.13	0.68	0.13	0.00
194	SFD1_01A	65.27	0.01	34.16	0.50	0.00	0.06
195	SFDH_02A	56.48	11.40	31.54	0.50	0.00	0.08
196	SFD3_03A	54.63	14.47	30.28	0.50	0.09	0.03
197	SFD3_04A	58.27	9.17	31.77	0.50	0.29	0.00
198	SFD__05A	57.98	0.01	41.34	0.55	0.01	0.11
199	SFD__06A	55.03	8.26	35.76	0.57	0.00	0.38

Results of TGA and Colors of the Powder Samples after Measuring
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C.
L_T : Total weight loss, L₄₀₀ : Weight loss of 400-1,000°C.
No. Name L_T
(wt%) L₄₀₀
(wt%) X Y Z Whiteness
(Hunter) L a b Whiteness
(Lab)
173 HFIH_01S 5.38 4.60 85.23 86.10 92.33 78.25 92.79 1.57 5.96 90.52
174 HFI2_02A 5.81 4.89 75.80 74.67 72.72 61.63 86.41 5.36 10.59 81.96
175 HFIN_03A 5.38 4.35 47.58 42.55 28.26 23.95 65.23 16.05 19.97 56.81
176 HFIN_04A 5.72 4.48 80.87 80.55 80.11 67.89 89.75 3.78 9.90 85.26
177 HFIN_06A 5.06 3.99 56.73 54.76 46.30 39.24 74.00 7.34 14.70 69.24
178 HFIN_08A 5.07 4.19 65.64 62.18 52.23 44.26 78.85 10.59 15.93 71.49
179 HFI1_09S 5.49 4.60 85.42 86.42 93.93 79.60 92.96 1.33 5.17 91.17
180 HFI3S10A 5.04 4.33 74.44 72.21 62.53 52.99 84.98 7.66 15.85 76.85
181 HFI3_12A 4.64 3.79 66.03 63.23 56.27 47.69 79.52 9.07 13.71 73.74
182 HFI1_13A 5.78 4.73 87.28 88.41 97.51 82.64 94.03 1.15 4.33 92.53
183 HFI4_14A 4.71 4.00 62.62 59.20 48.44 41.05 76.94 10.63 16.53 69.70
194 SFD1_01A 4.90 4.22 73.21 71.13 67.89 57.53 84.34 7.35 11.31 79.33
195 SFDH_02A 5.17 4.31 68.43 66.70 64.82 54.93 81.67 6.64 10.11 78.04
196 SFD3_03A 4.99 4.10 64.13 61.32 53.80 45.59 78.31 9.15 14.08 72.57
197 SFD3_04A 5.06 4.16 67.46 64.45 54.64 46.31 80.28 9.50 15.84 72.98
198 SFD__05A 5.33 4.41 85.26 86.17 93.46 79.20 92.83 1.50 5.29 90.97
199 SFD__06A 5.45 4.41 57.72 56.26 53.58 45.41 75.01 6.10 10.15 72.34

Results of TGA and Colors of the Powder Samples after Measuring
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C. L_T : Total weight loss, L₄₀₀ : Weight loss of 400-1,000°C.
No.	Name	L_T (wt%)	L₄₀₀ (wt%)	X	Y	Z	Whiteness (Hunter)	L	a	b	Whiteness (Lab)
173	HFIH_01S	5.38	4.60	85.23	86.10	92.33	78.25	92.79	1.57	5.96	90.52
174	HFI2_02A	5.81	4.89	75.80	74.67	72.72	61.63	86.41	5.36	10.59	81.96
175	HFIN_03A	5.38	4.35	47.58	42.55	28.26	23.95	65.23	16.05	19.97	56.81
176	HFIN_04A	5.72	4.48	80.87	80.55	80.11	67.89	89.75	3.78	9.90	85.26
177	HFIN_06A	5.06	3.99	56.73	54.76	46.30	39.24	74.00	7.34	14.70	69.24
178	HFIN_08A	5.07	4.19	65.64	62.18	52.23	44.26	78.85	10.59	15.93	71.49
179	HFI1_09S	5.49	4.60	85.42	86.42	93.93	79.60	92.96	1.33	5.17	91.17
180	HFI3S10A	5.04	4.33	74.44	72.21	62.53	52.99	84.98	7.66	15.85	76.85
181	HFI3_12A	4.64	3.79	66.03	63.23	56.27	47.69	79.52	9.07	13.71	73.74
182	HFI1_13A	5.78	4.73	87.28	88.41	97.51	82.64	94.03	1.15	4.33	92.53
183	HFI4_14A	4.71	4.00	62.62	59.20	48.44	41.05	76.94	10.63	16.53	69.70
194	SFD1_01A	4.90	4.22	73.21	71.13	67.89	57.53	84.34	7.35	11.31	79.33
195	SFDH_02A	5.17	4.31	68.43	66.70	64.82	54.93	81.67	6.64	10.11	78.04
196	SFD3_03A	4.99	4.10	64.13	61.32	53.80	45.59	78.31	9.15	14.08	72.57
197	SFD3_04A	5.06	4.16	67.46	64.45	54.64	46.31	80.28	9.50	15.84	72.98
198	SFD__05A	5.33	4.41	85.26	86.17	93.46	79.20	92.83	1.50	5.29	90.97
199	SFD__06A	5.45	4.41	57.72	56.26	53.58	45.41	75.01	6.10	10.15	72.34

Results of TMA and Colors of the Sintered Samples after Measuring
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W₁₀ : Contents of particles larger than 10µm, S_M : Maximum shrinkage, T₀ : Temperature at the maximum shrinkage, T₅ : Temperature at the expansion coefficient becomes 0.0005/°C, T_S5 : Temperature rectified using the correlative equation, T_SK : Nominal temperature equivalent to its SK.
No. Name W₁₀
(wt%) S_M
(%) T₀
(°C) T₅
(°C) T_S5
(°C) T_SK
(°C) SK X Y Z W
(Hunter) L a b W
(Lab)
173 HFIH_01S 41.9 5.14 1582 1591 1590 1652 29 76.86 78.42 92.43 78.33 88.56 -0.05 0.10 88.55
174 HFI2_02A 42.5 6.14 1541 1559 1557 1645 29- 66.63 67.90 73.85 62.58 82.40 0.13 4.54 81.82
175 HFIN_03A 44.8 4.71 1556 1561 1558 1645 29- 21.43 22.00 24.44 20.71 46.90 -0.53 1.94 46.87
176 HFIN_04A 46.5 4.32 1592 1598 1593 1653 29 65.84 67.26 76.50 64.83 82.01 -0.22 2.10 81.89
177 HFIN_06A 43.9 5.96 1472 1485 1482 1614 27+ 43.16 44.01 47.10 39.92 66.34 0.03 4.34 66.06
178 HFIN_08A 44.6 6.30 1534 1547 1544 1641 29- 49.80 50.74 55.61 47.13 71.23 0.14 3.58 71.01
179 HFI1_09S 45.1 4.44 1590 1598 1594 1653 29 77.85 79.46 93.48 79.22 89.14 -0.10 0.22 89.14
180 HFI3S10A 42.5 6.00 1485 1499 1497 1622 28- 65.07 66.58 74.81 63.40 81.60 -0.45 2.76 81.39
181 HFI3_12A 43.5 8.43 1475 1480 1477 1611 27 50.71 51.72 55.91 47.38 71.92 0.01 4.25 71.60
182 HFI1_13A 41.1 5.95 1599 1600 1599 1653 29+ 71.66 73.22 85.09 72.11 85.57 -0.26 0.94 85.54
183 HFI4_14A 45.5 4.12 1502 1523 1519 1632 28 52.46 53.51 59.63 50.53 73.15 0.00 2.87 73.00
194 SFD1_01A 46.0 5.11 1600 1600 1596 1653 29+ 67.95 69.68 79.76 67.59 83.47 -0.78 1.78 83.36
195 SFDH_02A 44.2 3.99 1561 1573 1570 1648 29 65.96 67.54 76.30 64.66 82.18 -0.56 2.48 82.00
196 SFD3_03A 43.1 5.85 1487 1499 1497 1622 28- 43.08 44.13 47.11 39.92 66.43 -0.50 4.46 66.13
197 SFD3_04A 45.7 5.75 1576 1583 1579 1650 29 55.66 56.87 64.49 54.65 75.41 -0.22 2.09 75.32
198 SFD__05A 44.6 4.82 1600 1600 1597 1653 29+ 75.07 76.62 89.70 76.02 87.53 -0.10 0.52 87.52
199 SFD__06A 52.1 5.98 1571 1575 1566 1648 29 35.76 36.45 39.21 33.23 60.37 0.07 3.76 60.20
Last updated: August 1997

Results of TMA and Colors of the Sintered Samples after Measuring
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g. W₁₀ : Contents of particles larger than 10µm, S_M : Maximum shrinkage, T₀ : Temperature at the maximum shrinkage, T₅ : Temperature at the expansion coefficient becomes 0.0005/°C, T_S5 : Temperature rectified using the correlative equation, T_SK : Nominal temperature equivalent to its SK.
No.	Name	W₁₀ (wt%)	S_M (%)	T₀ (°C)	T₅ (°C)	T_S5 (°C)	T_SK (°C)	SK	X	Y	Z	W (Hunter)	L	a	b	W (Lab)
173	HFIH_01S	41.9	5.14	1582	1591	1590	1652	29	76.86	78.42	92.43	78.33	88.56	-0.05	0.10	88.55
174	HFI2_02A	42.5	6.14	1541	1559	1557	1645	29-	66.63	67.90	73.85	62.58	82.40	0.13	4.54	81.82
175	HFIN_03A	44.8	4.71	1556	1561	1558	1645	29-	21.43	22.00	24.44	20.71	46.90	-0.53	1.94	46.87
176	HFIN_04A	46.5	4.32	1592	1598	1593	1653	29	65.84	67.26	76.50	64.83	82.01	-0.22	2.10	81.89
177	HFIN_06A	43.9	5.96	1472	1485	1482	1614	27+	43.16	44.01	47.10	39.92	66.34	0.03	4.34	66.06
178	HFIN_08A	44.6	6.30	1534	1547	1544	1641	29-	49.80	50.74	55.61	47.13	71.23	0.14	3.58	71.01
179	HFI1_09S	45.1	4.44	1590	1598	1594	1653	29	77.85	79.46	93.48	79.22	89.14	-0.10	0.22	89.14
180	HFI3S10A	42.5	6.00	1485	1499	1497	1622	28-	65.07	66.58	74.81	63.40	81.60	-0.45	2.76	81.39
181	HFI3_12A	43.5	8.43	1475	1480	1477	1611	27	50.71	51.72	55.91	47.38	71.92	0.01	4.25	71.60
182	HFI1_13A	41.1	5.95	1599	1600	1599	1653	29+	71.66	73.22	85.09	72.11	85.57	-0.26	0.94	85.54
183	HFI4_14A	45.5	4.12	1502	1523	1519	1632	28	52.46	53.51	59.63	50.53	73.15	0.00	2.87	73.00
194	SFD1_01A	46.0	5.11	1600	1600	1596	1653	29+	67.95	69.68	79.76	67.59	83.47	-0.78	1.78	83.36
195	SFDH_02A	44.2	3.99	1561	1573	1570	1648	29	65.96	67.54	76.30	64.66	82.18	-0.56	2.48	82.00
196	SFD3_03A	43.1	5.85	1487	1499	1497	1622	28-	43.08	44.13	47.11	39.92	66.43	-0.50	4.46	66.13
197	SFD3_04A	45.7	5.75	1576	1583	1579	1650	29	55.66	56.87	64.49	54.65	75.41	-0.22	2.09	75.32
198	SFD__05A	44.6	4.82	1600	1600	1597	1653	29+	75.07	76.62	89.70	76.02	87.53	-0.10	0.52	87.52
199	SFD__06A	52.1	5.98	1571	1575	1566	1648	29	35.76	36.45	39.21	33.23	60.37	0.07	3.76	60.20