XRD, TGA and TMA Charts (No.199)
No. | Name | Sampling date | Vein or deposit | Mining place | Mining company | Sampling place | Grade or sort |
---|---|---|---|---|---|---|---|
199 | SFD__06A | March 26,1981 | Fukami V. | Fukami | Shin-ei Tohseki | Inside drift | Colored, fine |
Colors of the milled samples | |||||||
---|---|---|---|---|---|---|---|
X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab) |
68.36 | 68.49 | 63.09 | 53.47 | 82.76 | 2.62 | 12.73 | 78.41 |
Chemical compositions (wt%) | ||||||||
---|---|---|---|---|---|---|---|---|
SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | Na2O | K2O | Ig.loss |
78.20 | 14.94 | 1.01 | 0.04 | 0.08 | 0.16 | 0.02 | 0.39 | 4.69 |
Mineral compositions (wt%) | |||||
---|---|---|---|---|---|
Q : Quartz | M : Sericite | K : Kaolin mineral | F : Feldspar | C : Calcite | S : Siderite |
55.03 | 8.26 | 35.76 | 0.57 | 0.00 | 0.38 |
Results of TGA and Colors of the Powder Samples after Measuring | |||||||||
---|---|---|---|---|---|---|---|---|---|
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1000°C.
LT : Total weight loss, L400 : Weight loss of 400-1000°C. | |||||||||
LT (wt%) | L400 (wt%) | X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab) |
5.45 | 4.41 | 57.72 | 56.26 | 53.58 | 45.41 | 75.01 | 6.10 | 10.15 | 72.34 |
Results of TMA and Colors of the Sintered Samples after Measuring | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W10 : Contents of particles larger than 10µm, SMax : Maximum shrinkage, T0 : Temperature at the maximum shrinkage, T5 : Temperature at the expansion coefficient becomes 0.0005/°C, TS5 : Temperature rectified using the correlative equation, TSK : Nominal temperature equivalent to its SK. | ||||||||||||||
W10 (wt%) | SMax (%) | T0 (°C) | T5 (°C) | TS5 (°C) | TSK (°C) | SK | X | Y | Z | W (Hunter) | L | a | b | W (Lab) |
52.1 | 5.98 | 1571 | 1575 | 1566 | 1648 | 29 | 35.76 | 36.45 | 39.21 | 33.23 | 60.37 | 0.07 | 3.76 | 60.20 |