XRD, TGA and TMA Charts (No.173)
| No. | Name | Sampling date | Vein or deposit | Mining place | Mining company | Sampling place | Grade or sort |
|---|---|---|---|---|---|---|---|
| 173 | HFIH_01S | March 26,1981 | Fukami V. | Fukami | Hisatsune Tohseki | Inside drift/right/forth working face | Henshoku (discoloration) |
| Colors of the milled samples | |||||||
|---|---|---|---|---|---|---|---|
| X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab) |
| 85.82 | 86.80 | 97.60 | 82.71 | 93.17 | 1.38 | 3.11 | 92.37 |
| Chemical compositions (wt%) | ||||||||
|---|---|---|---|---|---|---|---|---|
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | Na2O | K2O | Ig.loss |
| 79.03 | 14.87 | 0.20 | 0.04 | 0.05 | 0.13 | 0.07 | 0.48 | 4.75 |
| Mineral compositions (wt%) | |||||
|---|---|---|---|---|---|
| Q : Quartz | M : Sericite | K : Kaolin mineral | F : Feldspar | C : Calcite | S : Siderite |
| 61.80 | 0.01 | 37.69 | 0.50 | 0.00 | 0.00 |
| Results of TGA and Colors of the Powder Samples after Measuring | |||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1000°C.
LT : Total weight loss, L400 : Weight loss of 400-1000°C. LT (wt%) | L400 (wt%) | X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab)
| 5.38 | 4.60 | 85.23 | 86.10 | 92.33 | 78.25 | 92.79 | 1.57 | 5.96 | 90.52
| | |||||||||
| Results of TMA and Colors of the Sintered Samples after Measuring | ||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W10 : Contents of particles larger than 10µm, SMax : Maximum shrinkage, T0 : Temperature at the maximum shrinkage, T5 : Temperature at the expansion coefficient becomes 0.0005/°C, TS5 : Temperature rectified using the correlative equation, TSK : Nominal temperature equivalent to its SK. W10 | (wt%) SMax | (%) T0 | (°C) T5 | (°C) TS5 | (°C) TSK | (°C) SK | X | Y | Z | W | (Hunter) L | a | b | W | (Lab) 41.9 | 5.14 | 1582 | 1591 | 1590 | 1652 | 29 | 76.86 | 78.42 | 92.43 | 78.33 | 88.56 | -0.05 | 0.10 | 88.55
| | ||||||||||||||
| Back to the list of vein or deposit | Back to the list of grade or sort |