Pottery-Stone Database / Others

Others, 32 samples

Results of TGA & Colors of the powder samples after measuring

Results of TMA & Colors of the sintered samples after measuring

No. Name Sampling date Vein or deposit Mining place Mining company Sampling place Grade or sort
010 USG__10S July 16, 1980 Sarayama V. Gohtsu Ueda Tohseki Lower level/center-upper ?
011 USGN_12A June 11, 1981 Sarayama V. Gohtsu Ueda Tohseki Left in the drift, in the rock crevice Clay
012 USGN_13A June 11, 1981 Sarayama V. Gohtsu Ueda Tohseki Fault belt upper in the drift Clay
024 USDX_05A March 29, 1980 Sarayama V. Denbeekoba Ueda Tohseki ? Sludge of natural, can't use
036 USDN_17A June 11, 1981 Sarayama V. Denbeekoba Ueda Tohseki Second level/center Fault clay
041 USDX_22A November 15, 1983 Sarayama V. Denbeekoba Ueda Tohseki Site of rock mass Translucent quartz ?
045 USI_M06A July 16, 1980 Sarayama V. Iguchiyama Ueda Tohseki Center/interior Mn(+)
047 USI__08A March 30, 1982 Sarayama V. Iguchiyama Ueda Tohseki Cliff/right, upper of lower level ?
070 UST__04A March 30, 1982 Sarayama V. Toboshi Ueda Tohseki ? ?
071 UST__05A March 30, 1982 Sarayama V. Toboshi Ueda Tohseki ? ?
072 UST__06A March 30, 1982 Sarayama V. Toboshi Ueda Tohseki Center/right lower ?
073 UST__07A March 30, 1982 Sarayama V. Toboshi Ueda Tohseki Tip of Sarayama vein/right ?
080 USSN_04A March 30, 1982 Sarayama V. Tsurugigasako Ueda Tohseki Inside drift Clay
081 USS__05A March 30, 1982 Sarayama V. Tsurugigasako Ueda Tohseki Outside drift Black vein
089 USYN_01A November 15, 1983 Sarayama V. Yazirogura Ueda Tohseki ? Clay
087 UKHXP05A November 15, 1983 Kaigan V. Kadonosako Ueda Tohseki Outside drift FeS(++), can't use
096 KKS__07A July 16, 1980 Kaigan V. Shimizuotoshi Kiyama Tohseki In the factory of acid treatment Product, SK18
059 UMON_03A June 11, 1981 Murayama V. Odatoko Furuyashiki Ueda Tohseki Lower drift, lower working face/left wall Clay (1)
060 UMON_04A June 11, 1981 Murayama V. Odatoko Furuyashiki Ueda Tohseki Lower drift, lower working face/left wall Clay (2)
145 KGY__05A December 1, 1980 Murayama V. Uchiyama Kyoritsu Yogyo Tohge(pass) working face Half way to metamorphose into pottery stone
158 NMSN_04A November 15, 1983 Murayama V. Shinden Nishizima Tohseki Shinden drift White clay
167 NMY__06A March 26, 1981 Murayama V. Yamanokohira Nishizima Tohseki ? SK27 ?
192 MHH__06A December 1, 1980 Murayama V. Hikarigami Matsuzaki Tohseki Left vein Onikawa(iron oxide rich phase) and good quality
193 MHH__08A November 15, 1983 Murayama V. Hikarigami Matsuzaki Tohseki ? Sample for measurement SK by JIS method
207 HTKX_04A June 11, 1981 Tanosako V. Kyogamine Harada Tohseki Stock yard Waste rock
175 HFIN_03A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/right/forth working face Onikawa(iron oxide rich phase) clay
176 HFIN_04A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/right/forth working face Fault clay
177 HFIN_06A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/left/forth working face Fault clay
178 HFIN_08A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Inside drift/left/third working face Fault clay
183 HFI4_14A March 26, 1981 Fukami V. Fukami Hisatsune Tohseki Dressing plant Waste rock, separable fourth grade
199 SFD__06A March 26, 1981 Fukami V. Fukami Shin-ei Tohseki Inside drift Colored, fine
127 K_X__02A December 1, 1980 Uchida D. Sarayama Kiyama Tohseki In the factory Raw material for octopus trap

No.	Name	Sampling date	Vein or deposit	Mining place	Mining company	Sampling place	Grade or sort
010	USG__10S	July 16, 1980	Sarayama V.	Gohtsu	Ueda Tohseki	Lower level/center-upper	?
011	USGN_12A	June 11, 1981	Sarayama V.	Gohtsu	Ueda Tohseki	Left in the drift, in the rock crevice	Clay
012	USGN_13A	June 11, 1981	Sarayama V.	Gohtsu	Ueda Tohseki	Fault belt upper in the drift	Clay
024	USDX_05A	March 29, 1980	Sarayama V.	Denbeekoba	Ueda Tohseki	?	Sludge of natural, can't use
036	USDN_17A	June 11, 1981	Sarayama V.	Denbeekoba	Ueda Tohseki	Second level/center	Fault clay
041	USDX_22A	November 15, 1983	Sarayama V.	Denbeekoba	Ueda Tohseki	Site of rock mass	Translucent quartz ?
045	USI_M06A	July 16, 1980	Sarayama V.	Iguchiyama	Ueda Tohseki	Center/interior	Mn(+)
047	USI__08A	March 30, 1982	Sarayama V.	Iguchiyama	Ueda Tohseki	Cliff/right, upper of lower level	?
070	UST__04A	March 30, 1982	Sarayama V.	Toboshi	Ueda Tohseki	?	?
071	UST__05A	March 30, 1982	Sarayama V.	Toboshi	Ueda Tohseki	?	?
072	UST__06A	March 30, 1982	Sarayama V.	Toboshi	Ueda Tohseki	Center/right lower	?
073	UST__07A	March 30, 1982	Sarayama V.	Toboshi	Ueda Tohseki	Tip of Sarayama vein/right	?
080	USSN_04A	March 30, 1982	Sarayama V.	Tsurugigasako	Ueda Tohseki	Inside drift	Clay
081	USS__05A	March 30, 1982	Sarayama V.	Tsurugigasako	Ueda Tohseki	Outside drift	Black vein
089	USYN_01A	November 15, 1983	Sarayama V.	Yazirogura	Ueda Tohseki	?	Clay
087	UKHXP05A	November 15, 1983	Kaigan V.	Kadonosako	Ueda Tohseki	Outside drift	FeS(++), can't use
096	KKS__07A	July 16, 1980	Kaigan V.	Shimizuotoshi	Kiyama Tohseki	In the factory of acid treatment	Product, SK18
059	UMON_03A	June 11, 1981	Murayama V.	Odatoko Furuyashiki	Ueda Tohseki	Lower drift, lower working face/left wall	Clay (1)
060	UMON_04A	June 11, 1981	Murayama V.	Odatoko Furuyashiki	Ueda Tohseki	Lower drift, lower working face/left wall	Clay (2)
145	KGY__05A	December 1, 1980	Murayama V.	Uchiyama	Kyoritsu Yogyo	Tohge(pass) working face	Half way to metamorphose into pottery stone
158	NMSN_04A	November 15, 1983	Murayama V.	Shinden	Nishizima Tohseki	Shinden drift	White clay
167	NMY__06A	March 26, 1981	Murayama V.	Yamanokohira	Nishizima Tohseki	?	SK27 ?
192	MHH__06A	December 1, 1980	Murayama V.	Hikarigami	Matsuzaki Tohseki	Left vein	Onikawa(iron oxide rich phase) and good quality
193	MHH__08A	November 15, 1983	Murayama V.	Hikarigami	Matsuzaki Tohseki	?	Sample for measurement SK by JIS method
207	HTKX_04A	June 11, 1981	Tanosako V.	Kyogamine	Harada Tohseki	Stock yard	Waste rock
175	HFIN_03A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/right/forth working face	Onikawa(iron oxide rich phase) clay
176	HFIN_04A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/right/forth working face	Fault clay
177	HFIN_06A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/left/forth working face	Fault clay
178	HFIN_08A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Inside drift/left/third working face	Fault clay
183	HFI4_14A	March 26, 1981	Fukami V.	Fukami	Hisatsune Tohseki	Dressing plant	Waste rock, separable fourth grade
199	SFD__06A	March 26, 1981	Fukami V.	Fukami	Shin-ei Tohseki	Inside drift	Colored, fine
127	K_X__02A	December 1, 1980	Uchida D.	Sarayama	Kiyama Tohseki	In the factory	Raw material for octopus trap

Colors of the milled samples
No. Name X Y Z Whiteness
(Hunter) L a b Whiteness
(Lab)
010 USG__10S 67.37 67.03 55.99 47.45 81.87 3.61 16.76 75.05
011 USGN_12A 80.66 81.14 76.06 64.46 90.08 2.20 12.99 83.51
012 USGN_13A 75.85 76.28 71.48 60.58 87.34 2.18 12.61 82.00
024 USDX_05A 60.14 55.95 30.75 26.06 74.80 12.62 27.99 60.28
036 USDN_17A 81.28 82.29 76.89 65.16 90.71 1.19 13.24 83.78
041 USDX_22A 77.70 78.79 74.41 63.06 88.76 0.91 12.43 83.22
045 USI_M06A 84.47 86.26 92.95 78.77 92.88 -0.19 5.68 90.89
047 USI__08A 85.44 87.21 95.73 81.13 93.39 -0.11 4.59 91.95
070 UST__04A 79.94 79.81 77.93 66.04 89.34 3.39 10.82 84.44
071 UST__05A 80.39 80.66 82.25 69.70 89.81 2.61 8.57 86.43
072 UST__06A 72.50 71.35 60.29 51.09 84.47 5.39 16.81 76.49
073 UST__07A 73.12 72.08 59.09 50.08 84.90 5.16 18.16 75.82
080 USSN_04A 75.47 75.55 74.77 63.36 86.92 2.88 9.84 83.38
081 USS__05A 74.03 74.08 78.08 66.17 86.07 2.91 6.46 84.37
089 USYN_01A 85.09 86.17 91.26 77.34 92.83 1.17 6.69 90.12
087 UKHXP05A 73.94 74.61 83.44 70.71 86.38 1.64 3.19 85.91
096 KKS__07A 85.11 85.50 92.03 77.99 92.47 2.48 5.72 90.22
059 UMON_03A 67.38 67.49 62.64 53.08 82.15 2.64 12.30 78.17
060 UMON_04A 77.23 77.65 69.74 59.10 88.12 2.23 14.76 80.92
145 KGY__05A 68.69 68.13 57.70 48.90 82.54 4.10 16.33 75.74
158 NMSN_04A 82.02 82.81 90.49 76.69 91.00 1.64 4.74 89.70
167 NMY__06A 69.12 68.53 57.61 48.82 82.78 4.17 16.69 75.66
192 MHH__06A 70.21 68.96 56.58 47.95 83.04 5.59 17.73 74.83
193 MHH__08A 71.72 71.16 64.26 54.46 84.36 4.14 13.88 78.68
207 HTKX_04A 68.48 68.12 54.16 45.90 82.53 3.67 18.87 74.03
175 HFIN_03A 61.51 59.73 40.41 34.25 77.29 6.82 23.10 66.89
176 HFIN_04A 84.36 85.19 87.66 74.29 92.30 1.63 8.30 88.56
177 HFIN_06A 57.55 57.42 50.92 43.15 75.78 2.96 13.20 72.25
178 HFIN_08A 76.66 76.30 66.22 56.12 87.35 3.79 16.20 79.10
183 HFI4_14A 71.46 70.45 58.98 49.98 83.93 5.09 17.09 76.00
199 SFD__06A 68.36 68.49 63.09 53.47 82.76 2.62 12.73 78.41
127 K_X__02A 46.63 45.48 30.03 25.45 67.44 5.40 20.81 60.98

Colors of the milled samples
No.	Name	X	Y	Z	Whiteness (Hunter)	L	a	b	Whiteness (Lab)
010	USG__10S	67.37	67.03	55.99	47.45	81.87	3.61	16.76	75.05
011	USGN_12A	80.66	81.14	76.06	64.46	90.08	2.20	12.99	83.51
012	USGN_13A	75.85	76.28	71.48	60.58	87.34	2.18	12.61	82.00
024	USDX_05A	60.14	55.95	30.75	26.06	74.80	12.62	27.99	60.28
036	USDN_17A	81.28	82.29	76.89	65.16	90.71	1.19	13.24	83.78
041	USDX_22A	77.70	78.79	74.41	63.06	88.76	0.91	12.43	83.22
045	USI_M06A	84.47	86.26	92.95	78.77	92.88	-0.19	5.68	90.89
047	USI__08A	85.44	87.21	95.73	81.13	93.39	-0.11	4.59	91.95
070	UST__04A	79.94	79.81	77.93	66.04	89.34	3.39	10.82	84.44
071	UST__05A	80.39	80.66	82.25	69.70	89.81	2.61	8.57	86.43
072	UST__06A	72.50	71.35	60.29	51.09	84.47	5.39	16.81	76.49
073	UST__07A	73.12	72.08	59.09	50.08	84.90	5.16	18.16	75.82
080	USSN_04A	75.47	75.55	74.77	63.36	86.92	2.88	9.84	83.38
081	USS__05A	74.03	74.08	78.08	66.17	86.07	2.91	6.46	84.37
089	USYN_01A	85.09	86.17	91.26	77.34	92.83	1.17	6.69	90.12
087	UKHXP05A	73.94	74.61	83.44	70.71	86.38	1.64	3.19	85.91
096	KKS__07A	85.11	85.50	92.03	77.99	92.47	2.48	5.72	90.22
059	UMON_03A	67.38	67.49	62.64	53.08	82.15	2.64	12.30	78.17
060	UMON_04A	77.23	77.65	69.74	59.10	88.12	2.23	14.76	80.92
145	KGY__05A	68.69	68.13	57.70	48.90	82.54	4.10	16.33	75.74
158	NMSN_04A	82.02	82.81	90.49	76.69	91.00	1.64	4.74	89.70
167	NMY__06A	69.12	68.53	57.61	48.82	82.78	4.17	16.69	75.66
192	MHH__06A	70.21	68.96	56.58	47.95	83.04	5.59	17.73	74.83
193	MHH__08A	71.72	71.16	64.26	54.46	84.36	4.14	13.88	78.68
207	HTKX_04A	68.48	68.12	54.16	45.90	82.53	3.67	18.87	74.03
175	HFIN_03A	61.51	59.73	40.41	34.25	77.29	6.82	23.10	66.89
176	HFIN_04A	84.36	85.19	87.66	74.29	92.30	1.63	8.30	88.56
177	HFIN_06A	57.55	57.42	50.92	43.15	75.78	2.96	13.20	72.25
178	HFIN_08A	76.66	76.30	66.22	56.12	87.35	3.79	16.20	79.10
183	HFI4_14A	71.46	70.45	58.98	49.98	83.93	5.09	17.09	76.00
199	SFD__06A	68.36	68.49	63.09	53.47	82.76	2.62	12.73	78.41
127	K_X__02A	46.63	45.48	30.03	25.45	67.44	5.40	20.81	60.98

Chemical compositions (wt%)
No. Name SiO₂ Al₂O₃ Fe₂O₃ TiO₂ CaO MgO Na₂O K₂O Ig.loss
010 USG__10S 79.54 14.03 0.71 0.01 0.02 0.08 0.07 1.88 3.34
011 USGN_12A 82.47 12.56 0.36 0.01 0.09 0.11 0.05 1.94 2.00
012 USGN_13A 79.36 14.50 0.51 0.01 0.11 0.14 0.08 1.76 3.18
024 USDX_05A 75.96 15.57 1.44 0.01 0.08 0.11 0.08 4.18 2.17
036 USDN_17A 82.12 12.78 0.35 0.01 0.09 0.10 0.06 2.01 2.07
041 USDX_22A 79.56 14.17 0.55 0.01 0.06 0.13 0.12 2.75 2.36
045 USI_M06A 77.34 15.72 0.38 0.01 0.05 0.15 0.10 3.57 2.36
047 USI__08A 81.74 12.98 0.41 0.01 0.02 0.06 0.11 2.54 1.87
070 UST__04A 77.66 15.26 0.47 0.01 0.07 0.16 0.09 3.06 2.66
071 UST__05A 77.76 15.23 0.45 0.02 0.09 0.19 0.10 2.83 2.73
072 UST__06A 78.87 14.58 0.58 0.01 0.05 0.10 0.09 2.65 2.73
073 UST__07A 78.40 14.75 0.76 0.01 0.05 0.08 0.08 2.90 2.71
080 USSN_04A 80.31 13.47 0.64 0.01 0.10 0.17 0.07 2.74 2.11
081 USS__05A 81.01 13.28 0.63 0.01 0.06 0.09 0.08 2.49 2.13
089 USYN_01A 77.52 15.59 0.28 0.01 0.04 0.13 0.05 2.64 3.17
087 UKHXP05A 79.08 14.28 0.60 0.02 0.03 0.08 0.06 2.77 2.78
096 KKS__07A 77.11 14.87 0.34 0.02 0.04 0.05 2.48 3.41 1.58
059 UMON_03A 81.10 13.43 0.31 0.02 0.05 0.09 0.08 2.16 2.52
060 UMON_04A 78.73 14.98 0.44 0.02 0.08 0.10 0.08 2.59 2.77
145 KGY__05A 74.71 14.56 0.86 0.02 0.95 0.13 4.34 2.19 2.04
158 NMSN_04A 78.75 14.17 0.86 0.02 0.11 0.13 0.05 2.73 2.88
167 NMY__06A 78.26 14.59 0.82 0.02 0.46 0.09 0.06 2.29 3.15
192 MHH__06A 77.89 14.93 0.85 0.02 0.05 0.09 0.60 2.64 2.74
193 MHH__08A 77.75 15.09 0.75 0.02 0.02 0.16 0.15 3.17 2.52
207 HTKX_04A 80.88 13.42 0.67 0.04 0.04 0.08 0.10 1.96 2.60
175 HFIN_03A 77.74 14.72 1.65 0.03 0.08 0.08 0.06 0.52 4.72
176 HFIN_04A 78.50 14.97 0.39 0.04 0.13 0.15 0.07 0.36 4.67
177 HFIN_06A 78.63 14.14 0.86 0.03 0.12 0.18 0.14 1.11 4.21
178 HFIN_08A 78.94 14.54 0.68 0.03 0.08 0.08 0.08 0.76 4.40
183 HFI4_14A 78.82 14.62 0.66 0.03 0.07 0.05 0.15 1.09 4.19
199 SFD__06A 78.20 14.94 1.01 0.04 0.08 0.16 0.02 0.39 4.69
127 K_X__02A 68.50 18.29 3.11 0.11 0.27 0.38 0.31 3.52 4.62

Chemical compositions (wt%)
No.	Name	SiO₂	Al₂O₃	Fe₂O₃	TiO₂	CaO	MgO	Na₂O	K₂O	Ig.loss
010	USG__10S	79.54	14.03	0.71	0.01	0.02	0.08	0.07	1.88	3.34
011	USGN_12A	82.47	12.56	0.36	0.01	0.09	0.11	0.05	1.94	2.00
012	USGN_13A	79.36	14.50	0.51	0.01	0.11	0.14	0.08	1.76	3.18
024	USDX_05A	75.96	15.57	1.44	0.01	0.08	0.11	0.08	4.18	2.17
036	USDN_17A	82.12	12.78	0.35	0.01	0.09	0.10	0.06	2.01	2.07
041	USDX_22A	79.56	14.17	0.55	0.01	0.06	0.13	0.12	2.75	2.36
045	USI_M06A	77.34	15.72	0.38	0.01	0.05	0.15	0.10	3.57	2.36
047	USI__08A	81.74	12.98	0.41	0.01	0.02	0.06	0.11	2.54	1.87
070	UST__04A	77.66	15.26	0.47	0.01	0.07	0.16	0.09	3.06	2.66
071	UST__05A	77.76	15.23	0.45	0.02	0.09	0.19	0.10	2.83	2.73
072	UST__06A	78.87	14.58	0.58	0.01	0.05	0.10	0.09	2.65	2.73
073	UST__07A	78.40	14.75	0.76	0.01	0.05	0.08	0.08	2.90	2.71
080	USSN_04A	80.31	13.47	0.64	0.01	0.10	0.17	0.07	2.74	2.11
081	USS__05A	81.01	13.28	0.63	0.01	0.06	0.09	0.08	2.49	2.13
089	USYN_01A	77.52	15.59	0.28	0.01	0.04	0.13	0.05	2.64	3.17
087	UKHXP05A	79.08	14.28	0.60	0.02	0.03	0.08	0.06	2.77	2.78
096	KKS__07A	77.11	14.87	0.34	0.02	0.04	0.05	2.48	3.41	1.58
059	UMON_03A	81.10	13.43	0.31	0.02	0.05	0.09	0.08	2.16	2.52
060	UMON_04A	78.73	14.98	0.44	0.02	0.08	0.10	0.08	2.59	2.77
145	KGY__05A	74.71	14.56	0.86	0.02	0.95	0.13	4.34	2.19	2.04
158	NMSN_04A	78.75	14.17	0.86	0.02	0.11	0.13	0.05	2.73	2.88
167	NMY__06A	78.26	14.59	0.82	0.02	0.46	0.09	0.06	2.29	3.15
192	MHH__06A	77.89	14.93	0.85	0.02	0.05	0.09	0.60	2.64	2.74
193	MHH__08A	77.75	15.09	0.75	0.02	0.02	0.16	0.15	3.17	2.52
207	HTKX_04A	80.88	13.42	0.67	0.04	0.04	0.08	0.10	1.96	2.60
175	HFIN_03A	77.74	14.72	1.65	0.03	0.08	0.08	0.06	0.52	4.72
176	HFIN_04A	78.50	14.97	0.39	0.04	0.13	0.15	0.07	0.36	4.67
177	HFIN_06A	78.63	14.14	0.86	0.03	0.12	0.18	0.14	1.11	4.21
178	HFIN_08A	78.94	14.54	0.68	0.03	0.08	0.08	0.08	0.76	4.40
183	HFI4_14A	78.82	14.62	0.66	0.03	0.07	0.05	0.15	1.09	4.19
199	SFD__06A	78.20	14.94	1.01	0.04	0.08	0.16	0.02	0.39	4.69
127	K_X__02A	68.50	18.29	3.11	0.11	0.27	0.38	0.31	3.52	4.62

Mineral compositions (wt%)
No. Name Quartz Sericite Kaolin mineral Feldspar Calcite Siderite
010 USG__10S 56.00 9.07 33.82 0.85 0.00 0.26
011 USGN_12A 55.99 30.90 12.61 0.50 0.00 0.00
012 USGN_13A 64.25 10.18 24.81 0.76 0.00 0.00
024 USDX_05A 45.40 52.09 0.87 1.29 0.28 0.07
036 USDN_17A 55.68 33.14 10.68 0.50 0.00 0.00
041 USDX_22A 56.28 32.57 10.45 0.69 0.01 0.00
045 USI_M06A 58.49 31.77 8.97 0.68 0.00 0.09
047 USI__08A 60.61 31.80 6.91 0.63 0.00 0.05
070 UST__04A 56.16 35.04 7.14 1.21 0.32 0.13
071 UST__05A 55.68 32.21 11.02 1.03 0.00 0.06
072 UST__06A 56.35 28.06 14.67 0.86 0.00 0.06
073 UST__07A 56.42 30.31 12.61 0.60 0.00 0.06
080 USSN_04A 58.23 32.40 7.48 1.18 0.30 0.41
081 USS__05A 55.89 35.11 8.40 0.50 0.00 0.10
089 USYN_01A 57.10 16.31 25.72 0.87 0.00 0.00
087 UKHXP05A 60.86 26.27 11.36 1.39 0.00 0.12
096 KKS__07A 47.23 25.82 6.12 20.81 0.00 0.02
059 UMON_03A 60.45 23.19 15.35 0.88 0.00 0.13
060 UMON_04A 54.88 25.96 18.66 0.50 0.00 0.00
145 KGY__05A 38.71 17.70 2.24 39.69 1.66 0.00
158 NMSN_04A 55.35 30.28 12.96 0.56 0.22 0.63
167 NMY__06A 57.55 23.81 17.40 1.04 0.20 0.00
192 MHH__06A 54.64 27.70 13.53 4.10 0.03 0.00
193 MHH__08A 59.30 30.52 8.05 1.66 0.30 0.17
207 HTKX_04A 61.34 16.34 21.05 1.11 0.08 0.08
175 HFIN_03A 61.38 5.36 32.68 0.50 0.08 0.00
176 HFIN_04A 58.50 9.50 31.08 0.63 0.14 0.15
177 HFIN_06A 54.58 17.06 27.78 0.50 0.00 0.08
178 HFIN_08A 54.10 2.01 43.28 0.50 0.00 0.11
183 HFI4_14A 52.69 13.37 33.13 0.68 0.13 0.00
199 SFD__06A 55.03 8.26 35.76 0.57 0.00 0.38
127 K_X__02A 33.01 38.07 24.81 3.01 0.46 0.64

Mineral compositions (wt%)
No.	Name	Quartz	Sericite	Kaolin mineral	Feldspar	Calcite	Siderite
010	USG__10S	56.00	9.07	33.82	0.85	0.00	0.26
011	USGN_12A	55.99	30.90	12.61	0.50	0.00	0.00
012	USGN_13A	64.25	10.18	24.81	0.76	0.00	0.00
024	USDX_05A	45.40	52.09	0.87	1.29	0.28	0.07
036	USDN_17A	55.68	33.14	10.68	0.50	0.00	0.00
041	USDX_22A	56.28	32.57	10.45	0.69	0.01	0.00
045	USI_M06A	58.49	31.77	8.97	0.68	0.00	0.09
047	USI__08A	60.61	31.80	6.91	0.63	0.00	0.05
070	UST__04A	56.16	35.04	7.14	1.21	0.32	0.13
071	UST__05A	55.68	32.21	11.02	1.03	0.00	0.06
072	UST__06A	56.35	28.06	14.67	0.86	0.00	0.06
073	UST__07A	56.42	30.31	12.61	0.60	0.00	0.06
080	USSN_04A	58.23	32.40	7.48	1.18	0.30	0.41
081	USS__05A	55.89	35.11	8.40	0.50	0.00	0.10
089	USYN_01A	57.10	16.31	25.72	0.87	0.00	0.00
087	UKHXP05A	60.86	26.27	11.36	1.39	0.00	0.12
096	KKS__07A	47.23	25.82	6.12	20.81	0.00	0.02
059	UMON_03A	60.45	23.19	15.35	0.88	0.00	0.13
060	UMON_04A	54.88	25.96	18.66	0.50	0.00	0.00
145	KGY__05A	38.71	17.70	2.24	39.69	1.66	0.00
158	NMSN_04A	55.35	30.28	12.96	0.56	0.22	0.63
167	NMY__06A	57.55	23.81	17.40	1.04	0.20	0.00
192	MHH__06A	54.64	27.70	13.53	4.10	0.03	0.00
193	MHH__08A	59.30	30.52	8.05	1.66	0.30	0.17
207	HTKX_04A	61.34	16.34	21.05	1.11	0.08	0.08
175	HFIN_03A	61.38	5.36	32.68	0.50	0.08	0.00
176	HFIN_04A	58.50	9.50	31.08	0.63	0.14	0.15
177	HFIN_06A	54.58	17.06	27.78	0.50	0.00	0.08
178	HFIN_08A	54.10	2.01	43.28	0.50	0.00	0.11
183	HFI4_14A	52.69	13.37	33.13	0.68	0.13	0.00
199	SFD__06A	55.03	8.26	35.76	0.57	0.00	0.38
127	K_X__02A	33.01	38.07	24.81	3.01	0.46	0.64

Results of TGA and Colors of the Powder Samples after Measuring
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C.
L_T : Total weight loss, L₄₀₀ : Weight loss of 400-1,000°C.
No. Name L_T
(wt%) L₄₀₀
(wt%) X Y Z Whiteness
(Hunter) L a b Whiteness
(Lab)
010 USG__10S 3.87 3.13 59.00 55.10 46.46 39.37 74.23 11.98 14.85 67.94
011 USGN_12A 2.68 1.88 75.86 73.69 67.48 57.19 85.84 7.52 13.48 79.05
012 USGN_13A 3.75 3.02 69.96 67.46 62.49 52.96 82.13 8.31 12.38 76.73
024 USDX_05A 2.85 1.89 45.93 39.28 24.23 20.53 62.67 21.13 20.95 52.26
036 USDN_17A 2.75 1.93 76.76 75.09 68.43 57.99 86.65 6.47 13.84 79.72
041 USDX_22A 2.85 2.21 72.93 71.53 65.94 55.88 84.58 5.91 12.98 78.99
045 USI_M06A 2.81 2.23 80.46 81.39 86.01 72.89 90.22 1.32 6.63 88.11
047 USI__08A 2.32 1.77 83.80 84.65 89.41 75.77 92.01 1.57 6.79 89.40
070 UST__04A 3.57 2.49 77.08 75.68 74.45 63.09 86.99 5.92 10.16 82.47
071 UST__05A 3.62 2.55 80.93 80.91 82.97 70.31 89.95 3.19 8.28 86.60
072 UST__06A 3.30 2.56 66.39 62.73 54.33 46.04 79.20 11.02 14.77 72.21
073 UST__07A 3.16 2.53 65.09 60.91 49.16 41.66 78.04 12.29 17.28 69.47
080 USSN_04A 2.71 1.93 67.47 66.71 67.28 57.02 81.68 4.52 8.33 79.37
081 USS__05A 2.57 1.97 67.44 67.07 71.90 60.93 81.90 3.67 5.27 80.79
089 USYN_01A 4.08 3.00 85.59 86.51 96.18 81.51 93.01 1.49 3.80 91.91
087 UKHXP05A 3.26 2.62 75.90 75.35 79.18 67.10 86.80 4.17 6.68 84.63
096 KKS__07A 1.85 1.50 83.10 83.47 88.80 75.25 91.36 2.47 6.33 89.01
059 UMON_03A 2.99 2.38 73.98 72.02 67.09 56.86 84.86 7.09 12.53 79.11
060 UMON_04A 3.16 2.66 73.60 70.83 60.11 50.94 84.16 8.82 16.57 75.44
145 KGY__05A 2.41 1.90 57.59 53.89 42.24 35.80 73.41 11.57 17.27 66.25
158 NMSN_04A 3.42 2.72 65.06 64.44 70.06 59.37 80.27 4.19 4.45 79.35
167 NMY__06A 3.65 2.92 60.53 56.78 47.67 40.40 75.35 11.52 15.24 68.82
192 MHH__06A 3.13 2.57 59.33 55.70 45.48 38.54 74.63 11.29 16.11 67.90
193 MHH__08A 3.13 2.35 69.58 67.71 58.91 49.92 82.29 6.94 15.15 75.68
207 HTKX_04A 3.04 2.45 64.15 60.12 48.60 41.19 77.54 11.99 17.11 69.32
175 HFIN_03A 5.38 4.35 47.58 42.55 28.26 23.95 65.23 16.05 19.97 56.81
176 HFIN_04A 5.72 4.48 80.87 80.55 80.11 67.89 89.75 3.78 9.90 85.26
177 HFIN_06A 5.06 3.99 56.73 54.76 46.30 39.24 74.00 7.34 14.70 69.24
178 HFIN_08A 5.07 4.19 65.64 62.18 52.23 44.26 78.85 10.59 15.93 71.49
183 HFI4_14A 4.71 4.00 62.62 59.20 48.44 41.05 76.94 10.63 16.53 69.70
199 SFD__06A 5.45 4.41 57.72 56.26 53.58 45.41 75.01 6.10 10.15 72.34
127 K_X__02A 5.80 3.96 43.15 37.89 21.86 18.53 61.55 17.41 22.03 52.39

Results of TGA and Colors of the Powder Samples after Measuring
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C. L_T : Total weight loss, L₄₀₀ : Weight loss of 400-1,000°C.
No.	Name	L_T (wt%)	L₄₀₀ (wt%)	X	Y	Z	Whiteness (Hunter)	L	a	b	Whiteness (Lab)
010	USG__10S	3.87	3.13	59.00	55.10	46.46	39.37	74.23	11.98	14.85	67.94
011	USGN_12A	2.68	1.88	75.86	73.69	67.48	57.19	85.84	7.52	13.48	79.05
012	USGN_13A	3.75	3.02	69.96	67.46	62.49	52.96	82.13	8.31	12.38	76.73
024	USDX_05A	2.85	1.89	45.93	39.28	24.23	20.53	62.67	21.13	20.95	52.26
036	USDN_17A	2.75	1.93	76.76	75.09	68.43	57.99	86.65	6.47	13.84	79.72
041	USDX_22A	2.85	2.21	72.93	71.53	65.94	55.88	84.58	5.91	12.98	78.99
045	USI_M06A	2.81	2.23	80.46	81.39	86.01	72.89	90.22	1.32	6.63	88.11
047	USI__08A	2.32	1.77	83.80	84.65	89.41	75.77	92.01	1.57	6.79	89.40
070	UST__04A	3.57	2.49	77.08	75.68	74.45	63.09	86.99	5.92	10.16	82.47
071	UST__05A	3.62	2.55	80.93	80.91	82.97	70.31	89.95	3.19	8.28	86.60
072	UST__06A	3.30	2.56	66.39	62.73	54.33	46.04	79.20	11.02	14.77	72.21
073	UST__07A	3.16	2.53	65.09	60.91	49.16	41.66	78.04	12.29	17.28	69.47
080	USSN_04A	2.71	1.93	67.47	66.71	67.28	57.02	81.68	4.52	8.33	79.37
081	USS__05A	2.57	1.97	67.44	67.07	71.90	60.93	81.90	3.67	5.27	80.79
089	USYN_01A	4.08	3.00	85.59	86.51	96.18	81.51	93.01	1.49	3.80	91.91
087	UKHXP05A	3.26	2.62	75.90	75.35	79.18	67.10	86.80	4.17	6.68	84.63
096	KKS__07A	1.85	1.50	83.10	83.47	88.80	75.25	91.36	2.47	6.33	89.01
059	UMON_03A	2.99	2.38	73.98	72.02	67.09	56.86	84.86	7.09	12.53	79.11
060	UMON_04A	3.16	2.66	73.60	70.83	60.11	50.94	84.16	8.82	16.57	75.44
145	KGY__05A	2.41	1.90	57.59	53.89	42.24	35.80	73.41	11.57	17.27	66.25
158	NMSN_04A	3.42	2.72	65.06	64.44	70.06	59.37	80.27	4.19	4.45	79.35
167	NMY__06A	3.65	2.92	60.53	56.78	47.67	40.40	75.35	11.52	15.24	68.82
192	MHH__06A	3.13	2.57	59.33	55.70	45.48	38.54	74.63	11.29	16.11	67.90
193	MHH__08A	3.13	2.35	69.58	67.71	58.91	49.92	82.29	6.94	15.15	75.68
207	HTKX_04A	3.04	2.45	64.15	60.12	48.60	41.19	77.54	11.99	17.11	69.32
175	HFIN_03A	5.38	4.35	47.58	42.55	28.26	23.95	65.23	16.05	19.97	56.81
176	HFIN_04A	5.72	4.48	80.87	80.55	80.11	67.89	89.75	3.78	9.90	85.26
177	HFIN_06A	5.06	3.99	56.73	54.76	46.30	39.24	74.00	7.34	14.70	69.24
178	HFIN_08A	5.07	4.19	65.64	62.18	52.23	44.26	78.85	10.59	15.93	71.49
183	HFI4_14A	4.71	4.00	62.62	59.20	48.44	41.05	76.94	10.63	16.53	69.70
199	SFD__06A	5.45	4.41	57.72	56.26	53.58	45.41	75.01	6.10	10.15	72.34
127	K_X__02A	5.80	3.96	43.15	37.89	21.86	18.53	61.55	17.41	22.03	52.39

Results of TMA and Colors of the Sintered Samples after Measuring
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W₁₀ : Contents of particles larger than 10µm, S_M : Maximum shrinkage, T₀ : Temperature at the maximum shrinkage, T₅ : Temperature at the expansion coefficient becomes 0.0005/°C, T_S5 : Temperature rectified using the correlative equation, T_SK : Nominal temperature equivalent to its SK.
No. Name W₁₀
(wt%) S_M
(%) T₀
(°C) T₅
(°C) T_S5
(°C) T_SK
(°C) SK X Y Z W
(Hunter) L a b W
(Lab)
010 USG__10S 44.3 7.32 1464 1475 1472 1608 27 56.64 57.75 62.93 53.33 75.99 0.05 4.10 75.65
011 USGN_12A 48.0 7.86 1450 1471 1465 1604 27- 67.21 68.51 76.23 64.60 82.77 0.09 3.33 82.45
012 USGN_13A 46.3 6.74 1474 1487 1482 1614 27+ 64.93 66.12 74.26 62.93 81.31 0.23 2.77 81.11
024 USDX_05A 50.8 5.83 1388 1398 1390 1546 20+ 44.19 45.22 45.19 38.30 67.25 -0.38 7.23 66.46
036 USDN_17A 47.9 6.08 1448 1473 1467 1605 27 68.37 70.04 78.05 66.14 83.69 -0.63 3.29 83.35
041 USDX_22A 38.9 8.96 1425 1437 1438 1585 26 60.26 61.78 66.53 56.38 78.60 -0.70 4.84 78.05
045 USI_M06A 47.4 7.68 1433 1449 1444 1589 26+ 70.33 71.96 80.05 67.84 84.83 -0.46 3.43 84.44
047 USI__08A 32.3 9.15 1432 1449 1455 1597 27- 63.76 65.38 72.64 61.56 80.86 -0.75 3.34 80.55
070 UST__04A 43.7 7.66 1403 1420 1417 1569 26- 67.63 69.17 75.52 64.00 83.17 -0.39 4.38 82.60
071 UST__05A 47.5 6.61 1415 1428 1423 1573 26 69.74 71.38 78.49 66.52 84.49 -0.51 4.06 83.96
072 UST__06A 40.4 9.24 1422 1432 1432 1580 26 61.19 62.62 66.95 56.74 79.13 -0.46 5.23 78.48
073 UST__07A 37.6 8.17 1418 1427 1429 1578 26 53.75 55.17 59.09 50.08 74.28 -0.81 4.83 73.82
080 USSN_04A 50.6 6.85 1414 1422 1414 1567 26- 57.75 59.01 63.51 53.82 76.82 -0.24 4.75 76.33
081 USS__05A 53.6 7.15 1434 1440 1430 1579 26 54.91 56.11 60.67 51.42 74.91 -0.24 4.41 74.52
089 USYN_01A 41.7 6.52 1469 1489 1488 1617 27+ 75.67 76.67 88.19 74.74 87.56 1.03 1.58 87.42
087 UKHXP05A 43.6 6.15 1440 1446 1443 1589 26+ 56.78 57.58 64.37 54.55 75.88 0.77 2.82 75.70
096 KKS__07A 52.8 7.80 1317 1334 1325 1477 17 68.68 69.67 76.00 64.41 83.47 0.80 4.44 82.86
059 UMON_03A 50.6 7.41 1475 1489 1481 1613 27+ 67.93 69.50 78.15 66.23 83.37 -0.44 2.78 83.13
060 UMON_04A 47.1 7.01 1472 1485 1480 1612 27 65.31 66.88 74.78 63.37 81.78 -0.56 3.03 81.52
145 KGY__05A 42.4 7.18 1246 1257 1255 1386 13+ 46.23 46.15 42.88 36.34 67.93 2.59 10.13 66.27
158 NMSN_04A 48.9 7.16 1428 1435 1429 1578 26 48.55 49.29 53.24 45.12 70.21 0.58 4.18 69.91
167 NMY__06A 46.9 6.60 1454 1461 1456 1598 27- 55.19 56.56 61.32 51.97 75.21 -0.62 4.30 74.83
192 MHH__06A 49.2 7.74 1419 1425 1418 1570 26- 51.15 52.48 56.34 47.75 72.44 -0.74 4.60 72.05
193 MHH__08A 52.2 7.96 1422 1430 1421 1572 26 53.69 55.12 61.53 52.14 74.24 -0.84 2.83 74.07
207 HTKX_04A 49.4 8.71 1482 1490 1483 1614 27+ 63.02 64.49 70.38 59.64 80.31 -0.46 4.25 79.85
175 HFIN_03A 44.8 4.71 1556 1561 1558 1645 29- 21.43 22.00 24.44 20.71 46.90 -0.53 1.94 46.87
176 HFIN_04A 46.5 4.32 1592 1598 1593 1653 29 65.84 67.26 76.50 64.83 82.01 -0.22 2.10 81.89
177 HFIN_06A 43.9 5.96 1472 1485 1482 1614 27+ 43.16 44.01 47.10 39.92 66.34 0.03 4.34 66.06
178 HFIN_08A 44.6 6.30 1534 1547 1544 1641 29- 49.80 50.74 55.61 47.13 71.23 0.14 3.58 71.01
183 HFI4_14A 45.5 4.12 1502 1523 1519 1632 28 52.46 53.51 59.63 50.53 73.15 0.00 2.87 73.00
199 SFD__06A 52.1 5.98 1571 1575 1566 1648 29 35.76 36.45 39.21 33.23 60.37 0.07 3.76 60.20
127 K_X__02A 41.3 9.17 1306 1319 1318 1469 16+ 31.42 31.67 29.02 24.59 56.28 1.18 8.82 55.38
Last updated: August 1997

Results of TMA and Colors of the Sintered Samples after Measuring
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g. W₁₀ : Contents of particles larger than 10µm, S_M : Maximum shrinkage, T₀ : Temperature at the maximum shrinkage, T₅ : Temperature at the expansion coefficient becomes 0.0005/°C, T_S5 : Temperature rectified using the correlative equation, T_SK : Nominal temperature equivalent to its SK.
No.	Name	W₁₀ (wt%)	S_M (%)	T₀ (°C)	T₅ (°C)	T_S5 (°C)	T_SK (°C)	SK	X	Y	Z	W (Hunter)	L	a	b	W (Lab)
010	USG__10S	44.3	7.32	1464	1475	1472	1608	27	56.64	57.75	62.93	53.33	75.99	0.05	4.10	75.65
011	USGN_12A	48.0	7.86	1450	1471	1465	1604	27-	67.21	68.51	76.23	64.60	82.77	0.09	3.33	82.45
012	USGN_13A	46.3	6.74	1474	1487	1482	1614	27+	64.93	66.12	74.26	62.93	81.31	0.23	2.77	81.11
024	USDX_05A	50.8	5.83	1388	1398	1390	1546	20+	44.19	45.22	45.19	38.30	67.25	-0.38	7.23	66.46
036	USDN_17A	47.9	6.08	1448	1473	1467	1605	27	68.37	70.04	78.05	66.14	83.69	-0.63	3.29	83.35
041	USDX_22A	38.9	8.96	1425	1437	1438	1585	26	60.26	61.78	66.53	56.38	78.60	-0.70	4.84	78.05
045	USI_M06A	47.4	7.68	1433	1449	1444	1589	26+	70.33	71.96	80.05	67.84	84.83	-0.46	3.43	84.44
047	USI__08A	32.3	9.15	1432	1449	1455	1597	27-	63.76	65.38	72.64	61.56	80.86	-0.75	3.34	80.55
070	UST__04A	43.7	7.66	1403	1420	1417	1569	26-	67.63	69.17	75.52	64.00	83.17	-0.39	4.38	82.60
071	UST__05A	47.5	6.61	1415	1428	1423	1573	26	69.74	71.38	78.49	66.52	84.49	-0.51	4.06	83.96
072	UST__06A	40.4	9.24	1422	1432	1432	1580	26	61.19	62.62	66.95	56.74	79.13	-0.46	5.23	78.48
073	UST__07A	37.6	8.17	1418	1427	1429	1578	26	53.75	55.17	59.09	50.08	74.28	-0.81	4.83	73.82
080	USSN_04A	50.6	6.85	1414	1422	1414	1567	26-	57.75	59.01	63.51	53.82	76.82	-0.24	4.75	76.33
081	USS__05A	53.6	7.15	1434	1440	1430	1579	26	54.91	56.11	60.67	51.42	74.91	-0.24	4.41	74.52
089	USYN_01A	41.7	6.52	1469	1489	1488	1617	27+	75.67	76.67	88.19	74.74	87.56	1.03	1.58	87.42
087	UKHXP05A	43.6	6.15	1440	1446	1443	1589	26+	56.78	57.58	64.37	54.55	75.88	0.77	2.82	75.70
096	KKS__07A	52.8	7.80	1317	1334	1325	1477	17	68.68	69.67	76.00	64.41	83.47	0.80	4.44	82.86
059	UMON_03A	50.6	7.41	1475	1489	1481	1613	27+	67.93	69.50	78.15	66.23	83.37	-0.44	2.78	83.13
060	UMON_04A	47.1	7.01	1472	1485	1480	1612	27	65.31	66.88	74.78	63.37	81.78	-0.56	3.03	81.52
145	KGY__05A	42.4	7.18	1246	1257	1255	1386	13+	46.23	46.15	42.88	36.34	67.93	2.59	10.13	66.27
158	NMSN_04A	48.9	7.16	1428	1435	1429	1578	26	48.55	49.29	53.24	45.12	70.21	0.58	4.18	69.91
167	NMY__06A	46.9	6.60	1454	1461	1456	1598	27-	55.19	56.56	61.32	51.97	75.21	-0.62	4.30	74.83
192	MHH__06A	49.2	7.74	1419	1425	1418	1570	26-	51.15	52.48	56.34	47.75	72.44	-0.74	4.60	72.05
193	MHH__08A	52.2	7.96	1422	1430	1421	1572	26	53.69	55.12	61.53	52.14	74.24	-0.84	2.83	74.07
207	HTKX_04A	49.4	8.71	1482	1490	1483	1614	27+	63.02	64.49	70.38	59.64	80.31	-0.46	4.25	79.85
175	HFIN_03A	44.8	4.71	1556	1561	1558	1645	29-	21.43	22.00	24.44	20.71	46.90	-0.53	1.94	46.87
176	HFIN_04A	46.5	4.32	1592	1598	1593	1653	29	65.84	67.26	76.50	64.83	82.01	-0.22	2.10	81.89
177	HFIN_06A	43.9	5.96	1472	1485	1482	1614	27+	43.16	44.01	47.10	39.92	66.34	0.03	4.34	66.06
178	HFIN_08A	44.6	6.30	1534	1547	1544	1641	29-	49.80	50.74	55.61	47.13	71.23	0.14	3.58	71.01
183	HFI4_14A	45.5	4.12	1502	1523	1519	1632	28	52.46	53.51	59.63	50.53	73.15	0.00	2.87	73.00
199	SFD__06A	52.1	5.98	1571	1575	1566	1648	29	35.76	36.45	39.21	33.23	60.37	0.07	3.76	60.20
127	K_X__02A	41.3	9.17	1306	1319	1318	1469	16+	31.42	31.67	29.02	24.59	56.28	1.18	8.82	55.38