Pottery-Stone Database / Shima

Shima (Stripes) pottery stone, 14 samples

Results of TGA & Colors of the powder samples after measuring

Results of TMA & Colors of the sintered samples after measuring

No. Name Sampling date Vein or deposit Mining place Mining company Sampling place Grade or sort
015 USGS_17A November 13, 1982 Sarayama V. Gohtsu Ueda Tohseki Lower level/right Shima (stripes), Boundary of Tamamono (discoloration)
018 USGH_20A November 13, 1982 Sarayama V. Gohtsu Ueda Tohseki ? Shima- henshoku (stripes- discoloration)
019 USGH_21A November 13, 1982 Sarayama V. Gohtsu Ueda Tohseki ? =USGH_20A ?
033 USDS_14A June 11, 1981 Sarayama V. Denbeekoba Ueda Tohseki In factory of acid treatment High SK, Shima (stripes)
050 USIS_11A March 30, 1982 Sarayama V. Iguchiyama Ueda Tohseki ? White part in Shima (stripes)
069 USTS_03A March 30, 1982 Sarayama V. Toboshi Ueda Tohseki Upper of USTH_01A Shima (stripes)
056 UKMS_03A July 16, 1980 Kaigan V. Michitanosako Ueda Tohseki Stack Shima (stripes)
130 KKNS_03A November 15, 1983 Kaigan V. Niiyama Kiyama Tohseki Open cut Shima (stripes), raw material for acid treatment
150 KGYS_10A December 1, 1980 Murayama V. Gosoh Kyoritsu Yogyo East vein working face Shima (stripes)
153 KGYS_14A December 1, 1980 Murayama V. Uchiyama Kyoritsu Yogyo Lower working face =KGY__02S ?, deep Shima (stripes)
160 NMNS_02A March 26, 1981 Murayama V. Nihonmatsu Nishizima Tohseki Nihonmatsu drift Shima (stripes), pink color, SK20+-26
187 MHHS_01A December 1, 1980 Murayama V. Hikarigami Matsuzaki Tohseki ? Inferior, Shima (stripes), SK19
191 MHHS_05A December 1, 1980 Murayama V. Hikarigami Matsuzaki Tohseki ? Shima (stripes), SK19
218 OOY__11A June 11, 1981 Ooyano D. Ooyano Hashimoto Tohseki Waste dump of Kobayashi Shoji Co. Mokumeishi (stripes stone)

No.	Name	Sampling date	Vein or deposit	Mining place	Mining company	Sampling place	Grade or sort
015	USGS_17A	November 13, 1982	Sarayama V.	Gohtsu	Ueda Tohseki	Lower level/right	Shima (stripes), Boundary of Tamamono (discoloration)
018	USGH_20A	November 13, 1982	Sarayama V.	Gohtsu	Ueda Tohseki	?	Shima- henshoku (stripes- discoloration)
019	USGH_21A	November 13, 1982	Sarayama V.	Gohtsu	Ueda Tohseki	?	=USGH_20A ?
033	USDS_14A	June 11, 1981	Sarayama V.	Denbeekoba	Ueda Tohseki	In factory of acid treatment	High SK, Shima (stripes)
050	USIS_11A	March 30, 1982	Sarayama V.	Iguchiyama	Ueda Tohseki	?	White part in Shima (stripes)
069	USTS_03A	March 30, 1982	Sarayama V.	Toboshi	Ueda Tohseki	Upper of USTH_01A	Shima (stripes)
056	UKMS_03A	July 16, 1980	Kaigan V.	Michitanosako	Ueda Tohseki	Stack	Shima (stripes)
130	KKNS_03A	November 15, 1983	Kaigan V.	Niiyama	Kiyama Tohseki	Open cut	Shima (stripes), raw material for acid treatment
150	KGYS_10A	December 1, 1980	Murayama V.	Gosoh	Kyoritsu Yogyo	East vein working face	Shima (stripes)
153	KGYS_14A	December 1, 1980	Murayama V.	Uchiyama	Kyoritsu Yogyo	Lower working face	=KGY__02S ?, deep Shima (stripes)
160	NMNS_02A	March 26, 1981	Murayama V.	Nihonmatsu	Nishizima Tohseki	Nihonmatsu drift	Shima (stripes), pink color, SK20+-26
187	MHHS_01A	December 1, 1980	Murayama V.	Hikarigami	Matsuzaki Tohseki	?	Inferior, Shima (stripes), SK19
191	MHHS_05A	December 1, 1980	Murayama V.	Hikarigami	Matsuzaki Tohseki	?	Shima (stripes), SK19
218	OOY__11A	June 11, 1981	Ooyano D.	Ooyano	Hashimoto Tohseki	Waste dump of Kobayashi Shoji Co.	Mokumeishi (stripes stone)

Colors of the milled samples
No. Name X Y Z Whiteness
(Hunter) L a b Whiteness
(Lab)
015 USGS_17A 70.53 70.99 58.62 49.68 84.26 1.97 17.73 76.21
018 USGH_20A 73.67 73.32 61.88 52.44 85.63 3.73 17.09 77.36
019 USGH_21A 85.01 86.29 94.53 80.11 92.89 0.79 4.69 91.45
033 USDS_14A 74.22 74.31 58.59 49.65 86.20 2.83 20.04 75.50
050 USIS_11A 69.92 67.77 49.54 41.98 82.32 7.54 21.95 70.83
069 USTS_03A 76.35 75.36 67.33 57.06 86.81 5.07 14.78 79.55
056 UKMS_03A 71.17 70.32 54.65 46.31 83.86 4.74 20.06 73.82
130 KKNS_03A 65.46 64.55 51.98 44.05 80.34 4.83 17.88 72.99
150 KGYS_10A 67.39 66.64 49.20 41.69 81.63 4.50 21.41 71.44
153 KGYS_14A 62.24 61.46 48.02 40.69 78.40 4.52 18.56 71.16
160 NMNS_02A 66.61 65.95 52.14 44.19 81.21 4.29 18.78 73.09
187 MHHS_01A 70.27 67.47 59.51 50.43 82.14 8.96 14.54 75.29
191 MHHS_05A 70.28 68.95 54.96 46.58 83.04 5.77 18.88 73.97
218 OOY__11A 66.53 66.27 52.23 44.26 81.41 3.42 18.94 73.24

Colors of the milled samples
No.	Name	X	Y	Z	Whiteness (Hunter)	L	a	b	Whiteness (Lab)
015	USGS_17A	70.53	70.99	58.62	49.68	84.26	1.97	17.73	76.21
018	USGH_20A	73.67	73.32	61.88	52.44	85.63	3.73	17.09	77.36
019	USGH_21A	85.01	86.29	94.53	80.11	92.89	0.79	4.69	91.45
033	USDS_14A	74.22	74.31	58.59	49.65	86.20	2.83	20.04	75.50
050	USIS_11A	69.92	67.77	49.54	41.98	82.32	7.54	21.95	70.83
069	USTS_03A	76.35	75.36	67.33	57.06	86.81	5.07	14.78	79.55
056	UKMS_03A	71.17	70.32	54.65	46.31	83.86	4.74	20.06	73.82
130	KKNS_03A	65.46	64.55	51.98	44.05	80.34	4.83	17.88	72.99
150	KGYS_10A	67.39	66.64	49.20	41.69	81.63	4.50	21.41	71.44
153	KGYS_14A	62.24	61.46	48.02	40.69	78.40	4.52	18.56	71.16
160	NMNS_02A	66.61	65.95	52.14	44.19	81.21	4.29	18.78	73.09
187	MHHS_01A	70.27	67.47	59.51	50.43	82.14	8.96	14.54	75.29
191	MHHS_05A	70.28	68.95	54.96	46.58	83.04	5.77	18.88	73.97
218	OOY__11A	66.53	66.27	52.23	44.26	81.41	3.42	18.94	73.24

Chemical compositions (wt%)
No. Name SiO₂ Al₂O₃ Fe₂O₃ TiO₂ CaO MgO Na₂O K₂O Ig.loss
015 USGS_17A 77.24 15.08 0.72 0.01 0.15 0.13 1.33 2.20 2.73
018 USGH_20A 74.55 15.25 0.77 0.01 1.25 0.12 1.97 2.15 3.42
019 USGH_21A 73.36 15.09 0.83 0.01 1.95 0.12 1.99 2.22 4.03
033 USDS_14A 77.79 15.01 0.60 0.01 0.07 0.19 0.10 3.60 2.13
050 USIS_11A 77.51 15.28 0.85 0.01 0.05 0.15 0.10 3.11 2.57
069 USTS_03A 78.16 15.03 0.58 0.01 0.08 0.09 0.07 3.05 2.61
056 UKMS_03A 75.89 15.25 0.97 0.05 0.38 0.15 2.48 2.47 2.17
130 KKNS_03A 75.05 14.83 0.87 0.02 1.79 0.14 0.05 2.28 4.74
150 KGYS_10A 78.19 14.62 0.86 0.02 0.03 0.13 0.13 3.57 2.18
153 KGYS_14A 75.63 15.11 1.01 0.02 0.28 0.14 1.43 3.39 2.57
160 NMNS_02A 73.63 14.79 0.78 0.02 2.22 0.19 0.23 2.97 4.51
187 MHHS_01A 76.96 14.91 0.79 0.02 0.05 0.10 2.30 2.71 1.95
191 MHHS_05A 75.19 15.02 0.89 0.02 0.02 0.06 3.31 3.83 1.47
218 OOY__11A 72.08 15.06 1.09 0.07 2.11 0.22 1.98 3.13 3.91

Chemical compositions (wt%)
No.	Name	SiO₂	Al₂O₃	Fe₂O₃	TiO₂	CaO	MgO	Na₂O	K₂O	Ig.loss
015	USGS_17A	77.24	15.08	0.72	0.01	0.15	0.13	1.33	2.20	2.73
018	USGH_20A	74.55	15.25	0.77	0.01	1.25	0.12	1.97	2.15	3.42
019	USGH_21A	73.36	15.09	0.83	0.01	1.95	0.12	1.99	2.22	4.03
033	USDS_14A	77.79	15.01	0.60	0.01	0.07	0.19	0.10	3.60	2.13
050	USIS_11A	77.51	15.28	0.85	0.01	0.05	0.15	0.10	3.11	2.57
069	USTS_03A	78.16	15.03	0.58	0.01	0.08	0.09	0.07	3.05	2.61
056	UKMS_03A	75.89	15.25	0.97	0.05	0.38	0.15	2.48	2.47	2.17
130	KKNS_03A	75.05	14.83	0.87	0.02	1.79	0.14	0.05	2.28	4.74
150	KGYS_10A	78.19	14.62	0.86	0.02	0.03	0.13	0.13	3.57	2.18
153	KGYS_14A	75.63	15.11	1.01	0.02	0.28	0.14	1.43	3.39	2.57
160	NMNS_02A	73.63	14.79	0.78	0.02	2.22	0.19	0.23	2.97	4.51
187	MHHS_01A	76.96	14.91	0.79	0.02	0.05	0.10	2.30	2.71	1.95
191	MHHS_05A	75.19	15.02	0.89	0.02	0.02	0.06	3.31	3.83	1.47
218	OOY__11A	72.08	15.06	1.09	0.07	2.11	0.22	1.98	3.13	3.91

Mineral compositions (wt%)
No. Name Quartz Sericite Kaolin mineral Feldspar Calcite Siderite
015 USGS_17A 48.47 23.58 17.74 10.08 0.05 0.08
018 USGH_20A 43.01 25.51 13.18 16.03 2.20 0.07
019 USGH_21A 55.33 11.09 12.96 16.45 3.45 0.72
033 USDS_14A 52.37 43.34 3.61 0.50 0.18 0.00
050 USIS_11A 55.23 31.01 12.61 1.07 0.00 0.08
069 USTS_03A 54.36 29.48 14.55 1.61 0.00 0.00
056 UKMS_03A 46.02 23.02 8.97 21.98 0.00 0.01
130 KKNS_03A 52.93 22.51 20.25 1.14 3.16 0.01
150 KGYS_10A 60.32 34.56 3.27 1.64 0.08 0.13
153 KGYS_14A 43.97 29.22 12.27 13.89 0.50 0.15
160 NMNS_02A 44.30 37.30 13.53 0.58 3.95 0.34
187 MHHS_01A 55.41 18.41 5.32 20.71 0.15 0.00
191 MHHS_05A 38.45 28.02 1.90 31.63 0.00 0.00
218 OOY__11A 48.63 20.28 9.08 18.28 3.70 0.03

Mineral compositions (wt%)
No.	Name	Quartz	Sericite	Kaolin mineral	Feldspar	Calcite	Siderite
015	USGS_17A	48.47	23.58	17.74	10.08	0.05	0.08
018	USGH_20A	43.01	25.51	13.18	16.03	2.20	0.07
019	USGH_21A	55.33	11.09	12.96	16.45	3.45	0.72
033	USDS_14A	52.37	43.34	3.61	0.50	0.18	0.00
050	USIS_11A	55.23	31.01	12.61	1.07	0.00	0.08
069	USTS_03A	54.36	29.48	14.55	1.61	0.00	0.00
056	UKMS_03A	46.02	23.02	8.97	21.98	0.00	0.01
130	KKNS_03A	52.93	22.51	20.25	1.14	3.16	0.01
150	KGYS_10A	60.32	34.56	3.27	1.64	0.08	0.13
153	KGYS_14A	43.97	29.22	12.27	13.89	0.50	0.15
160	NMNS_02A	44.30	37.30	13.53	0.58	3.95	0.34
187	MHHS_01A	55.41	18.41	5.32	20.71	0.15	0.00
191	MHHS_05A	38.45	28.02	1.90	31.63	0.00	0.00
218	OOY__11A	48.63	20.28	9.08	18.28	3.70	0.03

Results of TGA and Colors of the Powder Samples after Measuring
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C.
L_T : Total weight loss, L₄₀₀ : Weight loss of 400-1,000°C.
No. Name L_T
(wt%) L₄₀₀
(wt%) X Y Z Whiteness
(Hunter) L a b Whiteness
(Lab)
015 USGS_17A 3.41 2.56 69.87 67.01 54.87 46.50 81.86 9.10 17.56 73.16
018 USGH_20A 4.14 3.21 65.54 62.02 50.11 42.47 78.75 10.73 17.40 70.51
019 USGH_21A 4.66 3.87 64.55 64.40 69.75 59.11 80.25 3.14 4.64 79.47
033 USDS_14A 2.84 1.93 62.47 57.75 43.09 36.52 75.99 13.75 19.58 66.11
050 USIS_11A 3.16 2.37 58.36 53.41 39.85 33.77 73.08 14.65 18.83 64.03
069 USTS_03A 3.14 2.47 72.10 69.85 65.34 55.37 83.58 7.73 12.15 78.16
056 UKMS_03A 2.56 1.99 61.93 57.05 38.64 32.75 75.53 14.18 22.54 63.84
130 KKNS_03A 5.14 4.50 55.26 50.62 38.77 32.86 71.15 14.13 17.49 63.42
150 KGYS_10A 2.75 1.97 56.22 51.35 36.09 30.58 71.66 14.64 20.30 62.19
153 KGYS_14A 3.29 2.36 59.10 54.55 39.35 33.35 73.86 13.58 20.11 64.33
160 NMNS_02A 5.47 4.26 59.25 54.67 37.48 31.76 73.94 13.64 21.70 63.44
187 MHHS_01A 2.32 1.79 64.80 61.64 48.76 41.32 78.51 9.93 18.14 70.18
191 MHHS_05A 1.83 1.25 62.43 58.48 43.96 37.25 76.47 11.90 19.45 67.24
218 OOY__11A 4.62 3.73 52.57 48.52 32.51 27.55 69.66 12.82 21.09 60.89

Results of TGA and Colors of the Powder Samples after Measuring
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C. L_T : Total weight loss, L₄₀₀ : Weight loss of 400-1,000°C.
No.	Name	L_T (wt%)	L₄₀₀ (wt%)	X	Y	Z	Whiteness (Hunter)	L	a	b	Whiteness (Lab)
015	USGS_17A	3.41	2.56	69.87	67.01	54.87	46.50	81.86	9.10	17.56	73.16
018	USGH_20A	4.14	3.21	65.54	62.02	50.11	42.47	78.75	10.73	17.40	70.51
019	USGH_21A	4.66	3.87	64.55	64.40	69.75	59.11	80.25	3.14	4.64	79.47
033	USDS_14A	2.84	1.93	62.47	57.75	43.09	36.52	75.99	13.75	19.58	66.11
050	USIS_11A	3.16	2.37	58.36	53.41	39.85	33.77	73.08	14.65	18.83	64.03
069	USTS_03A	3.14	2.47	72.10	69.85	65.34	55.37	83.58	7.73	12.15	78.16
056	UKMS_03A	2.56	1.99	61.93	57.05	38.64	32.75	75.53	14.18	22.54	63.84
130	KKNS_03A	5.14	4.50	55.26	50.62	38.77	32.86	71.15	14.13	17.49	63.42
150	KGYS_10A	2.75	1.97	56.22	51.35	36.09	30.58	71.66	14.64	20.30	62.19
153	KGYS_14A	3.29	2.36	59.10	54.55	39.35	33.35	73.86	13.58	20.11	64.33
160	NMNS_02A	5.47	4.26	59.25	54.67	37.48	31.76	73.94	13.64	21.70	63.44
187	MHHS_01A	2.32	1.79	64.80	61.64	48.76	41.32	78.51	9.93	18.14	70.18
191	MHHS_05A	1.83	1.25	62.43	58.48	43.96	37.25	76.47	11.90	19.45	67.24
218	OOY__11A	4.62	3.73	52.57	48.52	32.51	27.55	69.66	12.82	21.09	60.89

Results of TMA and Colors of the Sintered Samples after Measuring
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W₁₀ : Contents of particles larger than 10µm, S_M : Maximum shrinkage, T₀ : Temperature at the maximum shrinkage, T₅ : Temperature at the expansion coefficient becomes 0.0005/°C, T_S5 : Temperature rectified using the correlative equation, T_SK : Nominal temperature equivalent to its SK.
No. Name W₁₀
(wt%) S_M
(%) T₀
(°C) T₅
(°C) T_S5
(°C) T_SK
(°C) SK X Y Z W
(Hunter) L a b W
(Lab)
015 USGS_17A 43.4 6.61 1356 1372 1370 1526 20- 14.91 14.75 14.16 12.00 38.41 2.09 5.02 38.17
018 USGH_20A 46.5 7.32 1289 1298 1293 1438 15 58.89 59.59 60.77 51.50 77.19 1.08 7.36 76.01
019 USGH_21A 46.6 5.73 1286 1288 1283 1425 15- 48.88 49.45 53.16 45.05 70.32 1.01 4.40 69.98
033 USDS_14A 51.7 6.68 1413 1422 1413 1566 26- 62.08 63.60 68.98 58.46 79.75 -0.61 4.54 79.24
050 USIS_11A 44.7 5.41 1420 1426 1423 1573 26 56.31 57.73 60.51 51.28 75.98 -0.68 5.97 75.24
069 USTS_03A 51.9 7.55 1439 1448 1439 1586 26+ 64.17 65.73 71.89 60.92 81.07 -0.60 4.18 80.61
056 UKMS_03A 43.3 8.91 1302 1315 1313 1463 16 51.63 52.95 51.16 43.36 72.77 -0.69 9.25 71.23
130 KKNS_03A 43.9 6.23 1341 1347 1344 1499 18 53.73 54.97 55.54 47.07 74.14 -0.39 7.48 73.08
150 KGYS_10A 53.1 7.29 1424 1430 1420 1572 26- 54.90 56.02 59.02 50.02 74.85 -0.05 5.64 74.22
153 KGYS_14A 40.0 6.73 1323 1333 1333 1487 17+ 51.57 52.27 53.02 44.93 72.30 0.80 7.13 71.38
160 NMNS_02A 48.9 6.15 1323 1327 1321 1472 17- 58.71 59.53 60.34 51.14 77.16 0.80 7.64 75.90
187 MHHS_01A 50.2 8.26 1324 1335 1328 1480 17 56.34 57.65 59.94 50.80 75.93 -0.42 6.34 75.10
191 MHHS_05A 51.4 9.87 1275 1288 1280 1420 14+ 44.39 44.71 42.00 35.59 66.87 1.49 9.56 65.48
218 OOY__11A 50.2 8.08 1266 1274 1267 1402 14- 43.47 41.31 30.56 25.90 64.27 8.25 16.80 59.67
Last updated: August 1997

Results of TMA and Colors of the Sintered Samples after Measuring
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g. W₁₀ : Contents of particles larger than 10µm, S_M : Maximum shrinkage, T₀ : Temperature at the maximum shrinkage, T₅ : Temperature at the expansion coefficient becomes 0.0005/°C, T_S5 : Temperature rectified using the correlative equation, T_SK : Nominal temperature equivalent to its SK.
No.	Name	W₁₀ (wt%)	S_M (%)	T₀ (°C)	T₅ (°C)	T_S5 (°C)	T_SK (°C)	SK	X	Y	Z	W (Hunter)	L	a	b	W (Lab)
015	USGS_17A	43.4	6.61	1356	1372	1370	1526	20-	14.91	14.75	14.16	12.00	38.41	2.09	5.02	38.17
018	USGH_20A	46.5	7.32	1289	1298	1293	1438	15	58.89	59.59	60.77	51.50	77.19	1.08	7.36	76.01
019	USGH_21A	46.6	5.73	1286	1288	1283	1425	15-	48.88	49.45	53.16	45.05	70.32	1.01	4.40	69.98
033	USDS_14A	51.7	6.68	1413	1422	1413	1566	26-	62.08	63.60	68.98	58.46	79.75	-0.61	4.54	79.24
050	USIS_11A	44.7	5.41	1420	1426	1423	1573	26	56.31	57.73	60.51	51.28	75.98	-0.68	5.97	75.24
069	USTS_03A	51.9	7.55	1439	1448	1439	1586	26+	64.17	65.73	71.89	60.92	81.07	-0.60	4.18	80.61
056	UKMS_03A	43.3	8.91	1302	1315	1313	1463	16	51.63	52.95	51.16	43.36	72.77	-0.69	9.25	71.23
130	KKNS_03A	43.9	6.23	1341	1347	1344	1499	18	53.73	54.97	55.54	47.07	74.14	-0.39	7.48	73.08
150	KGYS_10A	53.1	7.29	1424	1430	1420	1572	26-	54.90	56.02	59.02	50.02	74.85	-0.05	5.64	74.22
153	KGYS_14A	40.0	6.73	1323	1333	1333	1487	17+	51.57	52.27	53.02	44.93	72.30	0.80	7.13	71.38
160	NMNS_02A	48.9	6.15	1323	1327	1321	1472	17-	58.71	59.53	60.34	51.14	77.16	0.80	7.64	75.90
187	MHHS_01A	50.2	8.26	1324	1335	1328	1480	17	56.34	57.65	59.94	50.80	75.93	-0.42	6.34	75.10
191	MHHS_05A	51.4	9.87	1275	1288	1280	1420	14+	44.39	44.71	42.00	35.59	66.87	1.49	9.56	65.48
218	OOY__11A	50.2	8.08	1266	1274	1267	1402	14-	43.47	41.31	30.56	25.90	64.27	8.25	16.80	59.67