Fourth grade pottery stone, 10 samples
Colors of the milled samples |
Chemical compositions |
Mineral compositions |
Results of TGA & Colors of the powder samples after measuring |
Results of TMA & Colors of the sintered samples after measuring |
No. | Name | Sampling date | Vein or deposit | Mining place | Mining company | Sampling place | Grade or sort |
---|---|---|---|---|---|---|---|
022 | USD4_03A | March 29, 1980 | Sarayama V. | Denbeekoba | Ueda Tohseki | ? | Fouth grade |
083 | USS4_07A | November 15, 1983 | Sarayama V. | Tsurugigasako | Ueda Tohseki | Kawanahata mine ? | Fourth grade |
074 | USKS401A | March 30, 1982 | Kaigan V. | Kawanohata | Ueda Tohseki | North | Fourth grade, Shima (stripes), SK20 |
076 | USKH403A | March 30, 1982 | Kaigan V. | Kawanohata | Ueda Tohseki | North | Fourth grade, Henshoku (discoloration), SK26 |
201 | HTO4_02A | June 11, 1981 | Kaigan V. | Ohsako | Harada Tohseki | Right wall | Good rock, Fourth grade? |
063 | UMOS407A | November 15, 1983 | Murayama V. | Odatoko Furuyashiki | Ueda Tohseki | Border between Nishizima Tohseki | Shima (stripes), fourth grade |
204 | HTKT401S | June 11, 1981 | Tanosako V. | Kyogamine | Harada Tohseki | Outside drift | Fourth grade, low SK |
107 | KGG4_03S | March 26, 1981 | Murayama V. | Gosoh | Kiyama Tohseki | Incline shaft working face | Fourth grade, SK19, kaolin / sericite=1 |
108 | KGG4_04A | March 26, 1981 | Murayama V. | Gosoh | Kiyama Tohseki | Incline shaft wall | Good rock of fourth grade, middle of bonanza |
109 | KGG4_05A | March 26, 1981 | Murayama V. | Gosoh | Kiyama Tohseki | Stock yard of incline shaft | Bad rock of fourth grade, SK16-17 |
Colors of the milled samples | |||||||||
---|---|---|---|---|---|---|---|---|---|
No. | Name | X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab) |
022 | USD4_03A | 71.94 | 71.91 | 59.00 | 50.00 | 84.80 | 3.03 | 18.11 | 76.16 |
083 | USS4_07A | 72.71 | 72.04 | 59.89 | 50.75 | 84.88 | 4.38 | 17.58 | 76.40 |
074 | USKS401A | 69.39 | 68.09 | 49.97 | 42.35 | 82.52 | 5.70 | 21.86 | 71.44 |
076 | USKH403A | 69.93 | 69.27 | 69.34 | 58.76 | 83.23 | 4.33 | 8.86 | 80.54 |
201 | HTO4_02A | 62.07 | 60.59 | 43.97 | 37.26 | 77.84 | 6.12 | 21.00 | 68.87 |
063 | UMOS407A | 83.62 | 83.72 | 84.98 | 72.02 | 91.50 | 3.01 | 8.98 | 87.27 |
204 | HTKT401S | 58.25 | 56.29 | 38.81 | 32.89 | 75.03 | 7.29 | 21.85 | 66.03 |
107 | KGG4_03S | 60.92 | 60.34 | 49.90 | 42.29 | 77.68 | 4.05 | 16.29 | 72.07 |
108 | KGG4_04A | 71.09 | 70.27 | 58.35 | 49.45 | 83.83 | 4.68 | 17.41 | 75.78 |
109 | KGG4_05A | 71.73 | 71.39 | 64.52 | 54.68 | 84.49 | 3.68 | 13.87 | 78.87 |
Chemical compositions (wt%) | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
No. | Name | SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | Na2O | K2O | Ig.loss |
022 | USD4_03A | 77.20 | 15.39 | 0.73 | 0.01 | 0.07 | 0.19 | 0.13 | 3.41 | 2.38 |
083 | USS4_07A | 79.97 | 13.93 | 0.56 | 0.01 | 0.06 | 0.07 | 0.07 | 2.94 | 2.10 |
074 | USKS401A | 77.40 | 15.12 | 0.77 | 0.01 | 0.09 | 0.11 | 0.09 | 3.36 | 2.57 |
076 | USKH403A | 76.90 | 15.35 | 0.78 | 0.01 | 0.08 | 0.16 | 0.07 | 3.80 | 2.36 |
201 | HTO4_02A | 75.83 | 14.59 | 1.40 | 0.05 | 0.06 | 0.11 | 4.19 | 2.27 | 1.31 |
063 | UMOS407A | 77.24 | 15.39 | 0.39 | 0.02 | 0.04 | 0.12 | 1.26 | 3.19 | 2.13 |
204 | HTKT401S | 76.13 | 14.95 | 1.25 | 0.05 | 0.09 | 0.06 | 3.14 | 2.08 | 2.04 |
107 | KGG4_03S | 75.22 | 14.39 | 0.75 | 0.01 | 1.15 | 0.11 | 2.33 | 3.35 | 2.47 |
108 | KGG4_04A | 77.26 | 14.67 | 0.72 | 0.01 | 0.88 | 0.09 | 0.05 | 2.06 | 4.03 |
109 | KGG4_05A | 74.55 | 14.56 | 0.69 | 0.01 | 0.93 | 0.05 | 3.02 | 3.94 | 2.10 |
Mineral compositions (wt%) | |||||||
---|---|---|---|---|---|---|---|
No. | Name | Quartz | Sericite | Kaolin mineral | Feldspar | Calcite | Siderite |
083 | USS4_07A | 54.44 | 36.53 | 8.51 | 0.50 | 0.00 | 0.02 |
074 | USKS401A | 60.79 | 24.59 | 13.30 | 1.03 | 0.25 | 0.04 |
076 | USKH403A | 58.83 | 34.07 | 5.09 | 1.20 | 0.41 | 0.40 |
201 | HTO4_02A | 47.41 | 8.32 | 1.56 | 42.36 | 0.35 | 0.00 |
063 | UMOS407A | 49.70 | 30.64 | 7.83 | 11.75 | 0.00 | 0.08 |
204 | HTKT401S | 42.73 | 16.39 | 7.60 | 33.28 | 0.00 | 0.00 |
107 | KGG4_03S | 42.97 | 22.18 | 8.85 | 23.95 | 2.05 | 0.00 |
108 | KGG4_04A | 51.23 | 24.26 | 22.42 | 0.50 | 1.59 | 0.00 |
109 | KGG4_05A | 32.72 | 33.76 | 4.98 | 26.90 | 1.64 | 0.00 |
Results of TGA and Colors of the Powder Samples after Measuring | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C.
LT : Total weight loss, L400 : Weight loss of 400-1,000°C. No. | Name | LT | (wt%) L400 | (wt%) X | Y | Z | Whiteness | (Hunter) L | a | b | Whiteness | (Lab) 022 | USD4_03A | 3.05 | 2.14 | 63.35 | 58.74 | 47.09 | 39.91 | 76.64 | 13.42 | 17.22 | 68.03
| 083 | USS4_07A | 2.65 | 1.94 | 63.82 | 59.51 | 48.13 | 40.79 | 77.14 | 12.67 | 17.01 | 68.82
| 074 | USKS401A | 3.26 | 2.33 | 61.85 | 57.14 | 40.23 | 34.09 | 75.59 | 13.77 | 21.36 | 64.76
| 076 | USKH403A | 3.31 | 2.16 | 62.80 | 62.10 | 64.55 | 54.70 | 78.80 | 4.34 | 6.60 | 77.38
| 201 | HTO4_02A | 1.77 | 1.08 | 48.84 | 44.06 | 30.05 | 25.47 | 66.38 | 15.18 | 19.62 | 58.22
| 063 | UMOS407A | 2.60 | 2.03 | 81.65 | 81.10 | 81.39 | 68.97 | 90.06 | 4.24 | 9.45 | 85.64
| 204 | HTKT401S | 2.43 | 1.80 | 47.17 | 41.85 | 27.87 | 23.62 | 64.69 | 16.94 | 19.74 | 56.14
| 107 | KGG4_03S | 2.85 | 2.27 | 57.17 | 53.09 | 40.29 | 34.14 | 72.86 | 12.55 | 18.22 | 64.99
| 108 | KGG4_04A | 4.44 | 3.83 | 58.57 | 54.38 | 45.07 | 38.19 | 73.74 | 12.72 | 15.38 | 67.02
| 109 | KGG4_05A | 2.38 | 1.97 | 64.62 | 61.88 | 52.59 | 44.57 | 78.66 | 8.97 | 15.43 | 72.18
| |
Results of TMA and Colors of the Sintered Samples after Measuring | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W10 : Contents of particles larger than 10µm, SM : Maximum shrinkage, T0 : Temperature at the maximum shrinkage, T5 : Temperature at the expansion coefficient becomes 0.0005/°C, TS5 : Temperature rectified using the correlative equation, TSK : Nominal temperature equivalent to its SK. No. | Name | W10 | (wt%) SM | (%) T0 | (°C) T5 | (°C) TS5 | (°C) TSK | (°C) SK | X | Y | Z | W | (Hunter) L | a | b | W | (Lab) 022 | USD4_03A | 40.3 | 7.79 | 1392 | 1400 | 1400 | 1554 | 20+ | 60.59 | 61.93 | 65.30 | 55.34 | 78.70 | -0.29 | 5.89 | 77.89
| 083 | USS4_07A | 47.7 | 8.82 | 1433 | 1444 | 1438 | 1585 | 26+ | 60.71 | 62.05 | 67.06 | 56.83 | 78.77 | -0.28 | 4.67 | 78.26
| 074 | USKS401A | 50.5 | 6.93 | 1419 | 1429 | 1421 | 1572 | 26 | 58.87 | 60.30 | 64.04 | 54.27 | 77.65 | -0.57 | 5.46 | 76.99
| 076 | USKH403A | 52.8 | 8.02 | 1391 | 1399 | 1390 | 1545 | 20+ | 55.82 | 57.12 | 60.82 | 51.54 | 75.58 | -0.43 | 5.19 | 75.03
| 201 | HTO4_02A | 50.4 | 9.27 | 1252 | 1263 | 1255 | 1387 | 13+ | 40.77 | 40.31 | 34.60 | 29.32 | 63.49 | 3.52 | 12.13 | 61.37
| 063 | UMOS407A | 47.9 | 7.83 | 1371 | 1386 | 1380 | 1536 | 20 | 71.43 | 73.05 | 79.79 | 67.62 | 85.47 | -0.39 | 4.48 | 84.79
| 204 | HTKT401S | 53.0 | 8.60 | 1273 | 1284 | 1275 | 1413 | 14 | 31.88 | 29.62 | 21.23 | 17.99 | 54.42 | 9.32 | 14.97 | 51.13
| 107 | KGG4_03S | 51.6 | 9.06 | 1259 | 1269 | 1261 | 1394 | 13+ | 50.95 | 51.08 | 51.86 | 43.95 | 71.47 | 2.18 | 7.01 | 70.54
| 108 | KGG4_04A | 47.1 | 5.63 | 1390 | 1399 | 1394 | 1549 | 20+ | 49.67 | 50.38 | 54.60 | 46.27 | 70.98 | 0.70 | 4.08 | 70.69
| 109 | KGG4_05A | 49.6 | 9.21 | 1237 | 1254 | 1247 | 1374 | 13- | 49.28 | 49.22 | 50.82 | 43.07 | 70.16 | 2.61 | 6.16 | 69.42
| |