First grade pottery stone, 7 samples
Colors of the milled samples |
Chemical compositions |
Mineral compositions |
Results of TGA & Colors of the powder samples after measuring |
Results of TMA & Colors of the sintered samples after measuring |
No. | Name | Sampling date | Vein or deposit | Mining place | Mining company | Sampling place | Grade or sort |
---|---|---|---|---|---|---|---|
042 | USI1_01A | March 29, 1980 | Sarayama V. | Iguchiyama | Ueda Tohseki | ? | First grade |
101 | KKS1_14A | June 11, 1981 | Kaigan V. | Shimizuotoshi | Kiyama Tohseki | Seashore | Recovery, first grade |
103 | KKS1_16A | June 11, 1981 | Kaigan V. | Shimizuotoshi | Kiyama Tohseki | ? | First grade B, small grain? |
058 | UMO1_02A | June 11, 1981 | Murayama V. | Odatoko Furuyashiki | Ueda Tohseki | Lower drift, upper working face/left wall | First grade |
179 | HFI1_09S | March 26, 1981 | Fukami V. | Fukami | Hisatsune Tohseki | Inside drift/left/second working face | First grade, SK29 |
182 | HFI1_13A | March 26, 1981 | Fukami V. | Fukami | Hisatsune Tohseki | Dressing plant | First grade, special grade in other vein |
194 | SFD1_01A | March 26, 1981 | Fukami V. | Fukami | Shin-ei Tohseki | Stock yard | First grade |
Colors of the milled samples | |||||||||
---|---|---|---|---|---|---|---|---|---|
No. | Name | X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab) |
042 | USI1_01A | 86.12 | 87.77 | 94.12 | 79.76 | 93.69 | 0.14 | 6.02 | 91.28 |
101 | KKS1_14A | 85.18 | 86.78 | 94.04 | 79.69 | 93.16 | 0.19 | 5.36 | 91.31 |
103 | KKS1_16A | 78.87 | 79.22 | 84.25 | 71.40 | 89.01 | 2.41 | 6.18 | 87.16 |
058 | UMO1_02A | 78.54 | 78.24 | 67.95 | 57.58 | 88.45 | 3.70 | 16.37 | 79.63 |
179 | HFI1_09S | 86.75 | 87.52 | 98.42 | 83.41 | 93.55 | 1.81 | 3.11 | 92.62 |
182 | HFI1_13A | 89.09 | 89.49 | 101.18 | 85.75 | 94.60 | 2.56 | 2.80 | 93.40 |
194 | SFD1_01A | 81.89 | 81.71 | 79.05 | 66.99 | 90.39 | 3.52 | 11.43 | 84.66 |
Chemical compositions (wt%) | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
No. | Name | SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | Na2O | K2O | Ig.loss |
042 | USI1_01A | 80.85 | 13.65 | 0.30 | 0.01 | 0.03 | 0.09 | 0.11 | 2.70 | 2.03 |
101 | KKS1_14A | 76.85 | 15.31 | 0.81 | 0.00 | 0.91 | 0.12 | 0.12 | 3.44 | 2.13 |
103 | KKS1_16A | 78.44 | 14.58 | 0.71 | 0.02 | 0.10 | 0.14 | 0.07 | 2.88 | 2.76 |
058 | UMO1_02A | 78.50 | 14.77 | 0.47 | 0.02 | 0.42 | 0.06 | 0.07 | 2.75 | 2.75 |
179 | HFI1_09S | 79.01 | 14.90 | 0.18 | 0.04 | 0.04 | 0.06 | 0.10 | 0.49 | 4.78 |
182 | HFI1_13A | 77.72 | 15.94 | 0.20 | 0.04 | 0.11 | 0.07 | 0.05 | 0.39 | 4.90 |
194 | SFD1_01A | 79.81 | 14.64 | 0.27 | 0.13 | 0.05 | 0.07 | 0.03 | 0.33 | 4.40 |
Mineral compositions (wt%) | |||||||
---|---|---|---|---|---|---|---|
No. | Name | Quartz | Sericite | Kaolin mineral | Feldspar | Calcite | Siderite |
042 | USI1_01A | 59.88 | 31.17 | 8.28 | 0.67 | 0.00 | 0.00 |
101 | KKS1_14A | 55.01 | 34.17 | 8.28 | 0.50 | 1.59 | 0.45 |
103 | KKS1_16A | 53.01 | 33.88 | 12.50 | 0.51 | 0.00 | 0.10 |
058 | UMO1_02A | 62.17 | 19.92 | 16.15 | 1.61 | 0.00 | 0.15 |
179 | HFI1_09S | 62.20 | 0.01 | 36.55 | 1.04 | 0.00 | 0.20 |
182 | HFI1_13A | 57.73 | 11.30 | 30.28 | 0.66 | 0.00 | 0.03 |
194 | SFD1_01A | 65.27 | 0.01 | 34.16 | 0.50 | 0.00 | 0.06 |
Results of TGA and Colors of the Powder Samples after Measuring | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C.
LT : Total weight loss, L400 : Weight loss of 400-1,000°C. No. | Name | LT | (wt%) L400 | (wt%) X | Y | Z | Whiteness | (Hunter) L | a | b | Whiteness | (Lab) 042 | USI1_01A | 2.39 | 1.94 | 85.17 | 86.06 | 92.12 | 78.07 | 92.77 | 1.53 | 6.06 | 90.44
| 101 | KKS1_14A | 2.68 | 1.98 | 82.57 | 82.61 | 85.80 | 72.71 | 90.89 | 3.10 | 7.65 | 87.70
| 103 | KKS1_16A | 3.32 | 2.59 | 65.97 | 65.47 | 71.35 | 60.47 | 80.91 | 3.94 | 4.36 | 80.03
| 058 | UMO1_02A | 3.13 | 2.64 | 68.59 | 64.92 | 55.29 | 46.86 | 80.57 | 10.95 | 15.72 | 72.72
| 179 | HFI1_09S | 5.49 | 4.60 | 85.42 | 86.42 | 93.93 | 79.60 | 92.96 | 1.33 | 5.17 | 91.17
| 182 | HFI1_13A | 5.78 | 4.73 | 87.28 | 88.41 | 97.51 | 82.64 | 94.03 | 1.15 | 4.33 | 92.53
| 194 | SFD1_01A | 4.90 | 4.22 | 73.21 | 71.13 | 67.89 | 57.53 | 84.34 | 7.35 | 11.31 | 79.33
| |
Results of TMA and Colors of the Sintered Samples after Measuring | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W10 : Contents of particles larger than 10µm, SM : Maximum shrinkage, T0 : Temperature at the maximum shrinkage, T5 : Temperature at the expansion coefficient becomes 0.0005/°C, TS5 : Temperature rectified using the correlative equation, TSK : Nominal temperature equivalent to its SK. No. | Name | W10 | (wt%) SM | (%) T0 | (°C) T5 | (°C) TS5 | (°C) TSK | (°C) SK | X | Y | Z | W | (Hunter) L | a | b | W | (Lab) 042 | USI1_01A | 44.9 | 7.98 | 1464 | 1477 | 1473 | 1609 | 27 | 70.68 | 72.40 | 81.92 | 69.42 | 85.09 | -0.63 | 2.48 | 84.87
| 101 | KKS1_14A | 51.5 | 6.54 | 1429 | 1438 | 1430 | 1579 | 26 | 73.46 | 74.22 | 83.01 | 70.35 | 86.15 | 1.44 | 3.18 | 85.72
| 103 | KKS1_16A | 50.0 | 6.31 | 1435 | 1442 | 1435 | 1583 | 26 | 57.82 | 58.62 | 63.46 | 53.78 | 76.56 | 0.81 | 4.45 | 76.13
| 058 | UMO1_02A | 48.7 | 7.17 | 1469 | 1480 | 1474 | 1609 | 27 | 62.55 | 64.06 | 71.64 | 60.71 | 80.04 | -0.57 | 2.96 | 79.81
| 179 | HFI1_09S | 45.1 | 4.44 | 1590 | 1598 | 1594 | 1653 | 29+ | 77.85 | 79.46 | 93.48 | 79.22 | 89.14 | -0.10 | 0.22 | 89.14
| 182 | HFI1_13A | 41.1 | 5.95 | 1599 | 1600 | 1599 | 1653 | 29+ | 71.66 | 73.22 | 85.09 | 72.11 | 85.57 | -0.26 | 0.94 | 85.54
| 194 | SFD1_01A | 46.0 | 5.11 | 1600 | 1600 | 1596 | 1653 | 29+ | 67.95 | 69.68 | 79.76 | 67.59 | 83.47 | -0.78 | 1.78 | 83.36
| |