Ooyano Deposit, 11 samples
Colors of the milled samples |
Chemical compositions |
Mineral compositions |
Results of TGA & Colors of the powder samples after measuring |
Results of TMA & Colors of the sintered samples after measuring |
No. | Name | Sampling date | Vein or deposit | Mining place | Mining company | Sampling place | Grade or sort |
---|---|---|---|---|---|---|---|
208 | OOY__01A | June 11, 1981 | Ooyano D. | Ooyano | Nihon Tohseki | Stock yard beside national road | Good quality |
209 | OOY__02A | June 11, 1981 | Ooyano D. | Ooyano | Nihon Tohseki | Stock yard beside national road | Bad quality |
210 | OOY__03A | June 11, 1981 | Ooyano D. | Ooyano | Nihon Tohseki | Stock yard beside national road | Bad quality, Shima(stripes) |
211 | OOY__04A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Top of deposit/center | Good quality ? |
212 | OOY__05A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Top of deposit/center | Bad quality, spot pattern |
213 | OOY__06A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Lower level/right | Good quality, white rock |
214 | OOY__07A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Lower level/right | Bad quality, brown |
215 | OOY__08A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Lower level/left | Good quality ? |
216 | OOY__09A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Waste dump of Amakusa pottery stone | Piece of griding stone |
217 | OOY__10A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Waste dump | Raw material of Iwao porcelain Co., Ltd., for tile ? |
218 | OOY__11A | June 11, 1981 | Ooyano D. | Ooyano | Hashimoto Tohseki | Waste dump of Kobayashi Shoji Co. | Mokumeishi(stripes stone) |
Colors of the milled samples | |||||||||
---|---|---|---|---|---|---|---|---|---|
No. | Name | X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab) |
208 | OOY__01A | 75.52 | 75.83 | 64.53 | 54.69 | 87.08 | 2.41 | 17.02 | 78.50 |
209 | OOY__02A | 75.33 | 76.09 | 64.01 | 54.25 | 87.23 | 1.50 | 17.55 | 78.24 |
210 | OOY__03A | 71.43 | 71.38 | 55.22 | 46.80 | 84.49 | 3.06 | 20.39 | 74.20 |
211 | OOY__04A | 76.83 | 77.92 | 76.79 | 65.08 | 88.27 | 0.89 | 10.21 | 84.42 |
212 | OOY__05A | 80.62 | 81.79 | 86.96 | 73.69 | 90.44 | 0.86 | 6.30 | 88.52 |
213 | OOY__06A | 72.03 | 71.90 | 54.84 | 46.47 | 84.79 | 3.24 | 21.01 | 73.86 |
214 | OOY__07A | 59.41 | 57.43 | 32.20 | 27.29 | 75.78 | 7.32 | 27.86 | 62.37 |
215 | OOY__08A | 79.92 | 81.02 | 82.43 | 69.86 | 90.01 | 0.97 | 8.71 | 86.71 |
216 | OOY__09A | 85.40 | 86.54 | 94.41 | 80.01 | 93.03 | 1.07 | 4.95 | 91.38 |
217 | OOY__10A | 75.12 | 75.73 | 65.66 | 55.64 | 87.02 | 1.79 | 16.18 | 79.18 |
218 | OOY__11A | 66.53 | 66.27 | 52.23 | 44.26 | 81.41 | 3.42 | 18.94 | 73.24 |
Chemical compositions (wt%) | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
No. | Name | SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | Na2O | K2O | Ig.loss |
208 | OOY__01A | 75.93 | 16.25 | 0.66 | 0.08 | 0.03 | 0.21 | 0.07 | 3.04 | 3.26 |
209 | OOY__02A | 76.05 | 15.81 | 0.80 | 0.08 | 0.06 | 0.24 | 0.06 | 3.22 | 3.07 |
210 | OOY__03A | 75.16 | 16.37 | 0.85 | 0.08 | 0.35 | 0.24 | 0.07 | 3.30 | 3.25 |
211 | OOY__04A | 75.54 | 15.39 | 0.82 | 0.08 | 0.07 | 0.30 | 2.72 | 2.87 | 1.81 |
212 | OOY__05A | 74.66 | 15.83 | 0.80 | 0.08 | 0.04 | 0.26 | 2.57 | 3.17 | 2.04 |
213 | OOY__06A | 75.68 | 16.04 | 0.90 | 0.08 | 0.06 | 0.27 | 0.09 | 3.27 | 3.03 |
214 | OOY__07A | 74.21 | 15.79 | 2.31 | 0.08 | 0.06 | 0.31 | 0.09 | 3.38 | 3.09 |
215 | OOY__08A | 75.58 | 16.25 | 0.56 | 0.08 | 0.07 | 0.30 | 0.11 | 3.38 | 3.09 |
216 | OOY__09A | 72.91 | 15.52 | 0.47 | 0.07 | 2.33 | 0.19 | 0.07 | 3.14 | 5.01 |
217 | OOY__10A | 75.87 | 16.27 | 0.71 | 0.08 | 0.03 | 0.27 | 0.06 | 3.23 | 3.20 |
218 | OOY__11A | 72.08 | 15.06 | 1.09 | 0.07 | 2.11 | 0.22 | 1.98 | 3.13 | 3.91 |
Mineral compositions (wt%) | |||||||
---|---|---|---|---|---|---|---|
No. | Name | Quartz | Sericite | Kaolin mineral | Feldspar | Calcite | Siderite |
208 | OOY__01A | 53.34 | 26.76 | 18.66 | 0.95 | 0.03 | 0.26 |
209 | OOY__02A | 54.15 | 26.55 | 18.77 | 0.50 | 0.00 | 0.03 |
210 | OOY__03A | 55.49 | 25.13 | 18.43 | 0.70 | 0.25 | 0.00 |
211 | OOY__04A | 46.69 | 23.77 | 2.35 | 27.08 | 0.11 | 0.00 |
212 | OOY__05A | 44.80 | 25.97 | 1.33 | 27.88 | 0.00 | 0.02 |
213 | OOY__06A | 54.53 | 32.23 | 12.73 | 0.51 | 0.00 | 0.00 |
214 | OOY__07A | 45.80 | 44.22 | 9.42 | 0.50 | 0.00 | 0.06 |
215 | OOY__08A | 50.04 | 33.36 | 15.01 | 1.36 | 0.23 | 0.00 |
216 | OOY__09A | 51.55 | 21.38 | 23.10 | 0.50 | 3.47 | 0.00 |
217 | OOY__10A | 55.80 | 20.31 | 22.42 | 1.25 | 0.00 | 0.22 |
218 | OOY__11A | 48.63 | 20.28 | 9.08 | 18.28 | 3.70 | 0.03 |
Results of TGA and Colors of the Powder Samples after Measuring | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C.
LT : Total weight loss, L400 : Weight loss of 400-1,000°C. No. | Name | LT | (wt%) L400 | (wt%) X | Y | Z | Whiteness | (Hunter) L | a | b | Whiteness | (Lab) 208 | OOY__01A | 4.05 | 3.05 | 68.34 | 65.16 | 52.10 | 44.15 | 80.72 | 9.86 | 18.24 | 71.69
| 209 | OOY__02A | 4.08 | 2.87 | 69.37 | 66.45 | 52.92 | 44.85 | 81.52 | 9.25 | 18.57 | 72.21
| 210 | OOY__03A | 3.85 | 3.09 | 62.63 | 58.38 | 44.57 | 37.77 | 76.41 | 12.60 | 18.90 | 67.25
| 211 | OOY__04A | 2.51 | 1.71 | 69.13 | 67.62 | 56.93 | 48.25 | 82.23 | 6.16 | 16.51 | 74.97
| 212 | OOY__05A | 2.95 | 1.90 | 72.57 | 72.43 | 66.10 | 56.02 | 85.11 | 3.27 | 13.52 | 79.62
| 213 | OOY__06A | 3.96 | 2.83 | 62.08 | 57.82 | 43.21 | 36.62 | 76.04 | 12.66 | 19.54 | 66.59
| 214 | OOY__07A | 4.13 | 2.70 | 46.13 | 39.65 | 20.27 | 17.18 | 62.97 | 20.57 | 24.99 | 50.81
| 215 | OOY__08A | 4.01 | 2.93 | 73.94 | 73.34 | 70.53 | 59.77 | 85.64 | 4.25 | 11.12 | 81.35
| 216 | OOY__09A | 5.56 | 4.89 | 77.00 | 77.32 | 82.78 | 70.15 | 87.93 | 2.43 | 5.74 | 86.42
| 217 | OOY__10A | 3.76 | 3.07 | 70.86 | 69.28 | 59.79 | 50.67 | 83.23 | 6.30 | 15.67 | 76.20
| 218 | OOY__11A | 4.62 | 3.73 | 52.57 | 48.52 | 32.51 | 27.55 | 69.66 | 12.82 | 21.09 | 60.89
| |
Results of TMA and Colors of the Sintered Samples after Measuring | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W10 : Contents of particles larger than 10µm, SM : Maximum shrinkage, T0 : Temperature at the maximum shrinkage, T5 : Temperature at the expansion coefficient becomes 0.0005/°C, TS5 : Temperature rectified using the correlative equation, TSK : Nominal temperature equivalent to its SK. No. | Name | W10 | (wt%) SM | (%) T0 | (°C) T5 | (°C) TS5 | (°C) TSK | (°C) SK | X | Y | Z | W | (Hunter) L | a | b | W | (Lab) 208 | OOY__01A | 46.5 | 7.69 | 1443 | 1451 | 1446 | 1591 | 26+ | 63.54 | 65.10 | 70.56 | 59.80 | 80.68 | -0.63 | 4.63 | 80.13
| 209 | OOY__02A | 48.4 | 8.21 | 1411 | 1421 | 1415 | 1567 | 26- | 57.94 | 59.29 | 64.05 | 54.28 | 77.00 | -0.43 | 4.58 | 76.54
| 210 | OOY__03A | 45.7 | 6.04 | 1433 | 1441 | 1437 | 1584 | 26 | 60.29 | 61.73 | 66.16 | 56.07 | 78.57 | -0.52 | 5.07 | 77.97
| 211 | OOY__04A | 45.7 | 6.70 | 1293 | 1306 | 1302 | 1449 | 16- | 56.22 | 57.39 | 58.02 | 49.17 | 75.76 | -0.11 | 7.62 | 74.59
| 212 | OOY__05A | 40.4 | 6.37 | 1294 | 1310 | 1310 | 1459 | 16 | 57.63 | 58.94 | 59.62 | 50.53 | 76.77 | -0.36 | 7.70 | 75.53
| 213 | OOY__06A | 51.2 | 6.14 | 1405 | 1414 | 1406 | 1560 | 26- | 56.59 | 57.94 | 61.46 | 52.08 | 76.12 | -0.50 | 5.41 | 75.51
| 214 | OOY__07A | 50.9 | 7.06 | 1369 | 1377 | 1369 | 1525 | 20- | 37.55 | 38.56 | 37.34 | 31.64 | 62.10 | -0.73 | 7.82 | 61.29
| 215 | OOY__08A | 45.9 | 6.21 | 1420 | 1432 | 1428 | 1577 | 26 | 67.19 | 68.71 | 75.30 | 63.81 | 82.89 | -0.37 | 4.16 | 82.39
| 216 | OOY__09A | 47.9 | 7.99 | 1340 | 1345 | 1339 | 1494 | 18- | 65.70 | 67.17 | 71.57 | 60.65 | 81.96 | -0.33 | 5.59 | 81.11
| 217 | OOY__10A | 46.6 | 9.69 | 1443 | 1452 | 1447 | 1592 | 26+ | 60.70 | 62.15 | 67.64 | 57.32 | 78.84 | -0.52 | 4.31 | 78.39
| 218 | OOY__11A | 50.2 | 8.08 | 1266 | 1274 | 1267 | 1402 | 14- | 43.47 | 41.31 | 30.56 | 25.90 | 64.27 | 8.25 | 16.80 | 59.67
| |