Binnomizu Vein, 3 samples
Colors of the milled samples |
Chemical compositions |
Mineral compositions |
Results of TGA & Colors of the powder samples after measuring |
Results of TMA & Colors of the sintered samples after measuring |
No. | Name | Sampling date | Vein or deposit | Mining place | Mining company | Sampling place | Grade or sort |
---|---|---|---|---|---|---|---|
064 | UBB__01A | March 30, 1982 | Binnomizu V. | Binnomizu | Ueda Tohseki | Lower level | Spot of sericite |
065 | UBB__02A | March 30, 1982 | Binnomizu V. | Binnomizu | Ueda Tohseki | Middle level | ? |
066 | UBB__03A | March 30, 1982 | Binnomizu V. | Binnomizu | Ueda Tohseki | Upper level | ? |
Colors of the milled samples | |||||||||
---|---|---|---|---|---|---|---|---|---|
No. | Name | X | Y | Z | Whiteness (Hunter) | L | a | b | Whiteness (Lab) |
064 | UBB__01A | 62.20 | 60.49 | 45.89 | 38.89 | 77.78 | 6.65 | 19.46 | 69.72 |
065 | UBB__02A | 70.92 | 70.27 | 65.09 | 55.16 | 83.83 | 4.32 | 12.64 | 79.02 |
066 | UBB__03A | 63.11 | 61.17 | 46.36 | 39.29 | 78.21 | 7.17 | 19.60 | 69.83 |
Chemical compositions (wt%) | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
No. | Name | SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | Na2O | K2O | Ig.loss |
064 | UBB__01A | 75.84 | 15.46 | 1.21 | 0.07 | 0.05 | 0.31 | 0.39 | 3.15 | 2.92 |
065 | UBB__02A | 76.45 | 15.03 | 0.95 | 0.07 | 0.02 | 0.26 | 1.70 | 3.00 | 2.13 |
066 | UBB__03A | 76.03 | 14.75 | 2.06 | 0.07 | 0.03 | 0.37 | 0.19 | 2.92 | 2.87 |
Mineral compositions (wt%) | |||||||
---|---|---|---|---|---|---|---|
No. | Name | Quartz | Sericite | Kaolin mineral | Feldspar | Calcite | Siderite |
064 | UBB__01A | 49.22 | 39.86 | 7.14 | 3.57 | 0.07 | 0.14 |
065 | UBB__02A | 49.31 | 32.70 | 3.27 | 14.63 | 0.00 | 0.09 |
066 | UBB__03A | 51.45 | 43.12 | 3.61 | 1.82 | 0.00 | 0.00 |
Results of TGA and Colors of the Powder Samples after Measuring | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TGA were sample weight : about 180mg, heating rate : 20°C/min, ended temperature : 1,000°C.
LT : Total weight loss, L400 : Weight loss of 400-1,000°C. No. | Name | LT | (wt%) L400 | (wt%) X | Y | Z | Whiteness | (Hunter) L | a | b | Whiteness | (Lab) 064 | UBB__01A | 3.79 | 2.53 | 51.18 | 46.80 | 36.44 | 30.88 | 68.41 | 13.82 | 16.31 | 61.86
| 065 | UBB__02A | 2.69 | 1.89 | 65.29 | 62.29 | 57.86 | 49.03 | 78.92 | 9.55 | 11.78 | 74.04
| 066 | UBB__03A | 3.82 | 2.42 | 49.94 | 45.24 | 34.69 | 29.40 | 67.26 | 14.83 | 16.50 | 60.45
| |
Results of TMA and Colors of the Sintered Samples after Measuring | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
The conditions for TMA were compaction pressure : 250MPa, pellet diameter : 10mm, thickness : about 3mm, heating rate : 10°C/min, loading : 10g.
W10 : Contents of particles larger than 10µm, SM : Maximum shrinkage, T0 : Temperature at the maximum shrinkage, T5 : Temperature at the expansion coefficient becomes 0.0005/°C, TS5 : Temperature rectified using the correlative equation, TSK : Nominal temperature equivalent to its SK. No. | Name | W10 | (wt%) SM | (%) T0 | (°C) T5 | (°C) TS5 | (°C) TSK | (°C) SK | X | Y | Z | W | (Hunter) L | a | b | W | (Lab) 064 | UBB__01A | 54.3 | 6.23 | 1362 | 1368 | 1358 | 1514 | 19- | 37.49 | 38.50 | 39.91 | 33.82 | 62.05 | -0.73 | 5.30 | 61.67
| 065 | UBB__02A | 49.8 | 7.73 | 1330 | 1341 | 1334 | 1488 | 17+ | 47.75 | 48.94 | 51.29 | 43.47 | 69.96 | -0.59 | 5.50 | 69.45
| 066 | UBB__03A | 42.4 | 7.57 | 1359 | 1366 | 1364 | 1520 | 19 | 34.17 | 34.92 | 34.86 | 29.54 | 59.09 | -0.20 | 6.39 | 58.60
| |